Grade BT25NPN has low moisture absorption and excellent dimensional stability.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.33 g/cm³ASTM D792Moisture absorption1.15 %ASTM D570Condition D₁-24/23MechanicalPropertyValueTesting StandardCommentCompressive modulus2.6 GPaASTM D695Condition

Grade BT25NEE is a tube made from a fine cotton fabric and an epoxy resin system. It has low moisture absorption and excellent dimensional stability and chemical resistance.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.33 g/cm³ASTM D792Moisture absorption0.9 %ASTM D570Condition D₁-24

Grade RTB324FR is constructed of a fine weave cotton fabric which has been bleached to remove impurities, and a modified phenolic resin with powdered PTFE added for lubrication as well as a flame retardant added. It has low moisture absorption and excellent dimensional stability and chemical resista

90%) and a NiFe binder phase.PropertiesGeneralPropertyTemperatureValueDensity23.0 °C18.25 - 18.85 g/cm³DimensionPropertyValueDiameter30 - 70 mmLength250 - 500 mmDimensionsAvailable dimensions (diameter x length, mm x mm): 30 x 500; 40 x 500; 70 x 250MechanicalPropertyTemperatureValueElongation23.0 °

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C13.25 g/cm³BinderCobalt binderGrain structureFine grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C4900 MPaElastic modulus23.0 °C530 GPaHardness, Rockwell A23.0 °C90.6 [-]Hardness,

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C12.45 g/cm³BinderCobalt binderGrain structureMedium grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C6000 MPaElastic modulus23.0 °C530 GPaHardness, Rockwell A23.0 °C91.5 [-]Hardness

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C12.2 g/cm³BinderCobalt binderGrain structureFine grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C5100 MPaElastic modulus23.0 °C505 GPaHardness, Rockwell A23.0 °C91.6 [-]Hardness, V

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C12.5 g/cm³BinderCobalt binderGrain structureMedium grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C5900 MPaElastic modulus23.0 °C505 GPaHardness, Rockwell A23.0 °C91.5 [-]Hardness,

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.45 g/cm³BinderCobalt binderGrain structureSubmicron grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C6600 MPaElastic modulus23.0 °C580 GPaHardness, Rockwell A23.0 °C92.3 [-]Hardn

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.6 g/cm³BinderCobalt binderGrain structureCoarse grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C4000 MPaElastic modulus23.0 °C580 GPaHardness, Rockwell A23.0 °C87.6 [-]Hardness,

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C11.6 g/cm³BinderCobalt binderGrain structureMedium grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C5300 MPaElastic modulus23.0 °C485 GPaHardness, Rockwell A23.0 °C90.2 [-]Hardness,

Tungsten hard material for wear protectionPropertiesGeneralPropertyTemperatureValueDensity23.0 °C14.15 g/cm³BinderCobalt binderGrain structureSubmicron grain sizeMechanicalPropertyTemperatureValueCompressive strength23.0 °C6100 MPaElastic modulus23.0 °C560 GPaHardness, Rockwell A23.0 °C90.9 [-]Hardn

Being a heat treated version of BT25NEE, BT25HEE is a tube made from a fine cotton fabric and an epoxy resin system. It has low moisture absorption and excellent dimensional stability and chemical resistance.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.32 g/cm³ASTM D792Moisture abso

NP515LS is a woven glass fabric combined with a high temperature phenolic resin. It is engineered to provide superior shrink characteristics at elevated temperatures, making it an ideal material for insulating gaskets. Having been tested and certified as a NEMA G-3 material, NP515LS also meets or ex

Materions AlBeCast® product line is a family of investment cast aluminum-beryllium metal matrix composites that provides designers a net-shape product. Advantages over aluminium A356.0: ~22% lower density ~3 times stiffer (modulus of elasticity in tension) Up to 10 times better in damping coefficien

Materions AlBeCast® product line is a family of investment cast aluminum-beryllium metal matrix composites that provides designers a net-shape product. Advantages over aluminium A356.0: ~22% lower density ~3 times stiffer (modulus of elasticity in tension) Up to 10 times better in damping coefficien

BP45NPM is composed of a 17 oz. aramid and soft glass fibers are combined to make a fabric that is stronger than pure aramid and less abrasive than glass fabrics. This material is impregnated with a high temperature phenolic resin matrix which includes a non-conducting solid lubricant. This composit

RT507F is manufactured using a fine weave glass fabric combined with a silicone resin system. It has excellent electrical properties under humid conditions, superior heat and arc resistance. The fine weave fabric substrate provides a “finer” finish on the surface of the finished part. RT507F also co

Grade BT25NPP is constructed of a fine weave cotton fabric which has been bleached to remove impurities, and a modified phenolic resin with powdered PTFE added for lubrication. It has low moisture absorption and excellent dimensional stability and chemical resistance.PropertiesGeneralPropertyValueTe

Being a heat treated version of BT25NPN, BT25HPN has low moisture absorption and excellent dimensional stability.PropertiesGeneralPropertyValueTesting StandardCommentDensity1.31 g/cm³ASTM D792Moisture absorption1.1 %ASTM D570Condition D₁-24/23MechanicalPropertyValueTesting StandardCommentCompressive