The cold-upsettable steel 19 MnB 4 can be cold-formed in rolling-hard condition with a low to medium forming rate and in the heat-treated conditions GKZ and K+GKZ+K with a high forming degree. It is used in the un-annealed condition for hexagon screws and hexagon socket head cap screws of the streng

The cold-upsettable steel Cq 15 is suitable for the manufacture of screws, nuts and small parts (valve spring plates, bearing sleeves) used in automobile, motor and equipment construction and in general engineering. For lower requirements and smaller sections, carbon steel is sufficient if the requ

Aluminum ASTM 6063 is an architectural alloy that offers users a high resistance to corrosion and excellent finishing characteristics. Easy to extrude with fair machinability, ASTM 6063 can be both hot and cold formed and is commonly available as T6 temper as well as T4 temper.PropertiesGeneralPrope

ASTM 6061 is a readily available alloy that has good surface finish and ability to be anodized.Easy of weldability and brazability with nice surface finish. Resistance to corrosion from seawater and atmospheric conditions. Suitable for hot forging.Quantity: 1 PCSPropertiesGeneralPropertyValueComment

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.9 g/cm³DimensionPropertyValueDimensionsDurchmesserMechanicalPropertyTemperatureValueElastic modulus20.0 °C112 GPaElongation20.0 °C30 %Hardness, Brinell20.0 °C65 - 90 [-]Hardness, Vickers20.0 °C70 - 95 [-]Tensile strength20.0 °C200 MPaYield str

Material EN AW-Al Cu5,5MgMn is food-safe and used for extruded and drawn components.PropertiesGeneralPropertyValueRelated StandardsShapeDensity2.82 g/cm³EN 573-3Strip, Sheet, Plate, Tube, BarMechanicalPropertyValueCommentElastic modulus70.0 - 73.0 GPaTypical for Wrought 2000 Series AluminiumPlane-St

AA 6020 is a wrought alloy that offers users good joining characteristics. This strong alloy has excellent corrosion resistance, machinability, and responds well to anodizing. Because AA 6020 is lead-free, it often replaces Aluminum 6262 in situations where higher levels of environmental safety are

The stainless steel X 7 CrNiAl 17 7 is usually used cold strained as wire up to 10 mm diameter or strip up to 1,6 mm thickness for springs or spring parts, also under corrosion stress and little raised temperatures.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.92 g/cm³MechanicalPropertyTe

The case-hardening steel is mainly used for gear parts, but also in the mechanical engineering.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon S

The steel 51 CrMoV 4 is used for hot formed springs, like high loaded car torsion springs, helical springs, tension springs and compression springs.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 - 7.85 g/cm³MechanicalPropertyTemperatureValueElastic modulus-100.0 °C217 GPa20.0 °C210 - 21

The steel 50 CrV 4 is used for hot formed springs like high loaded car plate springs, coil springs, torsion springs, helical springs and conical springs. High temperature strength up to 300 °C (valve springs). Assembly strength 1370 - 1720 N/mm².PropertiesGeneralPropertyTemperatureValueDensity20.0 °

The steel C 15 Pb is used for parts with a little higher core strength and better machinability in the vehicle and mechanical engineering (e.g. pins, lever, driver). The lowest application amounts to -25 °C, the best application from 5 to 10 mm nominal size.PropertiesGeneralPropertyTemperatureValueD

The steel is used for welded round link chains and chain components.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0

The steel is used for welded round link chains and chain components.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0

The steel is used for welded round link chains and chain components.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0

The steel is used for welded round link chains and chain components.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.82 - 7.83 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 - 208 GPa200.0 °C199 - 201 GPa300.0 °C192 - 193 GPa400.0 °C184

The steel is used for welded round link chains and chain components.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.84 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 - 208 GPa200.0 °C199 - 201 GPa300.0 °C192 - 193 GPa400.0 °C184 - 185

G-Ni95 possesses good corrosion-resistance to non-oxidizing mediums. The material shows very good resistance to hot and concentrated caustic alkalies as well as to dry gases, e.g. chlorine. G-Ni95 is applied in the chemical industry and in the food industry, for valves and fittings, apparatus parts,

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelPoisson's ratio23.0 °C0.29 [-]Typical for Low Carbon SteelShear modulus23.0 °C82 GPaTy

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelPoisson's ratio23.0 °C0.29 [-]Typical for Low Carbon SteelShear modulus23.0 °C82 GPaTy