JIS 6061 is a readily available alloy that has good surface finish and ability to be anodized.Easy of weldability and brazability with nice surface finish. Resistance to corrosion from seawater and atmospheric conditions. Suitable for hot forging.Quantity: 1 PCSPropertiesGeneralPropertyValueCommentD

Aluminum JIS 2024, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.PropertiesGeneralPr

Aluminum JIS 2017 is a heat treatable wrought alloy that offers decent strength, ductility, and good machinability. Aluminum JIS 2017 offers more strength than Aluminum 2011, and has fair workability and corrosion resistance. As with many aluminum alloys, Aluminum JIS 2017 should not be welded as it

JIS 7075 is a high-strength alloy that offers good stress-corrosion cracking resistance. Known as a mainstay in the aerospace industry since it was introduced, Aluminum 7075 brings moderate toughness as well as an excellent strength-to-weight ratio. It is also important to note that at sub-zero temp

JIS 7075 is a high-strength alloy that offers good stress-corrosion cracking resistance. Known as a mainstay in the aerospace industry since it was introduced, Aluminum 7075 brings moderate toughness as well as an excellent strength-to-weight ratio. It is also important to note that at sub-zero temp

Aluminum JIS 6063 is an architectural alloy that offers users a high resistance to corrosion and excellent finishing characteristics. Easy to extrude with fair machinability, JIS 6063 can be both hot and cold formed and is commonly available as T6 temper as well as T4 temper.PropertiesGeneralPropert

JIS 6061 is a readily available alloy that has good surface finish and ability to be anodized.Easy of weldability and brazability with nice surface finish. Resistance to corrosion from seawater and atmospheric conditions. Suitable for hot forging.Quantity: 1 PCSPropertiesGeneralPropertyValueCommentD

Aluminum JIS 2024, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.PropertiesGeneralPr

Aluminum JIS 2024, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.PropertiesGeneralPr

Aluminum JIS 3003 is a popular alloy that offers customers very good atmospheric corrosion resistance and moderate strength. Aluminum 3003 offers good machinability for aluminum alloys, though it is not heat treatable. Unlike other aluminum alloys, JIS 3003 is weldable by conventional welding method

Aluminum JIS 3003 is a popular alloy that offers customers very good atmospheric corrosion resistance and moderate strength. Aluminum 3003 offers good machinability for aluminum alloys, though it is not heat treatable. Unlike other aluminum alloys, JIS 3003 is weldable by conventional welding method

PropertiesGeneralPropertyValueCommentDensity2.75 - 2.84 g/cm³Typical for Wrought 2000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsCommentElastic modulus70.0 - 73.0 GPaTypical for Wrought 2000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 200

PropertiesGeneralPropertyValueCommentDensity2.75 - 2.84 g/cm³Typical for Wrought 2000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsCommentElastic modulus70.0 - 73.0 GPaTypical for Wrought 2000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 200

The material ZP5 with the material number ZP0410 is the preferred alloy for pressure castings. In its property profile, the alloy combines good mechanical properties with good resistance to corrosion, good dimensional accuracy und stability of accurate dimensions as well as with the possibility to g

The material ZP3 with the material number ZP0400 is applied for pressure castings. If high demands are made on the dimensional accuracy of the pressure casting products, this alloy ought to be preferably used. The material possesses considerably higher ductility than the other alloys. In comparison

Titanium DIN TiAl6V4 alloy is the most commercially available of all titanium alloys. It offers an excellent combination of high strength and toughness. DIN TiAl6V4 titanium has good welding and fabrication characteristics.PropertiesGeneralPropertyTemperatureValueConditionRelated StandardsShapeDensi

Material X46Cr13 is comparable to X 46 Cr 13 acc. to DIN 17440 : 1985-07. The material is used for the production of cutting tools (knife blades, scissors, cutting surgical instruments), ball bearing balls, abrasion resistant components for controlling and pump parts, springs, piston rods, screws. A

X60CrMnMoVNbN21-10 is an austenitic Cr-Mn-Mo-V-Nb-N-alloyed valve steel. The steel shows high corrosion resistance in exhaust condensate and very good resistance to lead compounds at increased temperatures. Application at operating temperatures up to 780 deg. Use: inlet valves, exhaust valvesPropert

Complete austenitic special steel for the application up to 800 °C with resistance to scaling up to 800 °C. It is unsensitive to embrittlement. Application: turbine and steam vessel manufacturing, hot-work tools as well as steel for high-pressure hydrogenation vessels at elevated temperaturesPropert

Complete austenitic special steel for the application up to 700 °C with resistance to scaling up to 800 °C. Application: turbine and steam vessel manufacturing (blades, valves, bolts etc.), parts in reactors as well as in the chemicals industryPropertiesGeneralPropertyTemperatureValueDensity20.0 °C8