PropertiesGeneralPropertyValueConditionRelated StandardsShapeDensity2.7 g/cm³FEN 573-3, EN 14121Strip, Sheet, PlateMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus70.0 GPaFEN 573-3, EN 14121Strip, Sheet, PlatePlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wro

PropertiesGeneralPropertyValueConditionRelated StandardsShapeDensity2.7 g/cm³T6BS 1474Bar, Tube, PlateMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus70 GPaT6BS 1474Bar, Tube, PlateElongation6.0 - 8.0 %T6BS 1474Bar, Tube, PlateHardness, Brinell84.0 - 91.0 [-]T6BS 14

PropertiesGeneralPropertyTemperatureValueDensity23.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C190 - 210 GPaIn Normalized ConditionElongation23.0 °C7 - 18 %For Different ConditionsHardness, Brinell23.0 °C197 [-]Hardness, Rockwell B23.0 °C92 [-]Poisson's ratio23.

Properties: - modification of 1.4571 - stainless extra low carbon-steel (ELC) - resistant to intergranular attack up to 550 °C Application: - for steel chimneyPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.77 - 8 g/cm³MechanicalPropertyTemperatureValueElastic modulus-100.0 °C206 GPa20.0 °C

Properties: - Cr-steel for quenching and tempering - elevated corrosion resistance - widely resistant in most organic and inorganic acids - relatively resistant in seawater - improved resistance to crevice corrosion - elevated heat resistance up to 600 °C - high polishable - use differnent quenched

Properties: - austenitic CrNi-steel with lowered Cr and Ni content, thus in case of cold forming occurs strongly hardening - sufficient corrosion resistance paired with high strength Application: - in cases there is demanded sufficient corrosion resistance paired with high strength - beater bar and

The ferritic-pearlitic, precipitation hardened steel 49 MnVS 3 is used for forgings and long products in the automotive industry.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0

The high temperature alloy steel X12CrMoWVNbN10-1-1 is used for larger preshaped components in the quenched and tempered condition in turbine and generator installations, in particular as shafts and discs. The steel is weldable if the relevant measures required are observed.PropertiesGeneralProperty

The high temperature alloy steel 23CrNiMo7-4-7 is used for larger preshaped components in the quenched and tempered condition in turbine and generator installations, in particular as shafts and discs. The steel is weldable if the relevant measures required are observed.PropertiesGeneralPropertyTempe

For components in furnace and apparatus engineering for high working temperatures, no embrittlement risk in the critical temperature range from 600 to 850 °C. (highest application temperature in air 1100 °C).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.98 - 8 g/cm³MechanicalPropertyTempe

Steel X3CrAlTi18-2 shows a highest application temperature of up to 1000 °C in air.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.7 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C220 GPaTypical for Ferritic Stainless SteelElongation20.0 °C25 %Elongation A8020.0 °C25 %H

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.84 g/cm³T61AA Standards, ASTM B247MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus69.0 - 72.0 GPaTypical for Wrought 7000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 7000 S

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.7 g/cm³T6511AA Standards, ASTM B221, ASTM B241MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 6

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.7 g/cm³T6510AA Standards, ASTM B221, ASTM B241MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 6

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.7 g/cm³T6AA Standards, ASTM B221, ASTM B241MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 6000

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.7 g/cm³T5511AA Standards, ASTM B241MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 6000 Series

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.7 g/cm³T5510AA Standards, ASTM B241MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 6000 Series

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.7 g/cm³T5AA Standards, ASTM B221, ASTM B241MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 6000

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.69 g/cm³T5AA Standards, ASTM B221MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 6000 Series Al

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.69 g/cm³T1AA Standards, ASTM B221MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 6000 Series Al