St 37-2 is used for moderate loaded parts, without inspection.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0 °C164

St 37-2 is used for moderate loaded parts, without inspection.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0 °C164

St 37-2 is used for moderate loaded parts, without inspection.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0 °C164

RZSt 37-2 as bright drawn grade is used stress dependent for welded constructions up to a temperature of -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °

RSt 37-2 is used stress dependent for welded constructions up to a temperature of -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa

The balanced machining steel 9 SMn 36 is used for higher demands on the cutting capacity and surface condition. The steel shows a elevated crack sensitivity. Application: limited in the automotive engineering, toolbuilding, apparatus engineeringPropertiesGeneralPropertyTemperatureValueDensity20.0 °C

Balanced machining steel 9 SMn 28 is the standard grade for all mass turning tools and should be the substitution of the 9 S 20. The steel is suited for thin walled parts and little cold forming. Application: automotive engineering, toolbuilding, apparatus engineeringPropertiesGeneralPropertyTempera

The fully killed machining steel 15 S 10 is applicated in the case hardened condition for thin walled parts with higher toughness demands. Application: automotive engineering, toolbuilding, apparatus engineeringPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemper

The fully killed machining steel 10 S 20 shows a better machinability with relative well toughness than the 15 S 10 and the 10 S 20. Application in the case hardened condition for thin-walled parts in the automotive engineering, toolbuilding, apparatus engineering.PropertiesGeneralPropertyTemperatur

G-AlSi7Mg - universal alloy with vers good mechanical properties, high strength and good toughness, very good corrosion resistance - excellent weldability application: -cast pieces in automobile, machine and aircraft industry, ship constructing and electrical engineeringPropertiesGeneralPropertyTemp

The structural steel S245G (unalloyed high-grade steel) will be supplied as cold rolled (usually skin passed and oiled) flat product (sheet and strip) without coating up to thicknesses of 3 mm.The weldability is given for commonon procedures.The suitability for coatings is given.PropertiesGeneralPro

The structural steel S215G (unalloyed high-grade steel) will be supplied as cold rolled (usually skin passed and oiled) flat product (sheet and strip) without coating up to thicknesses of 3 mm.The weldability is given for commonon procedures.The suitability for coatings is given.PropertiesGeneralPro

High temperature quenched and tempered steel. Application: larger forgings for mechanical engineering, steam vessels, pressure vesselsPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.82 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa

In comparison to the unalloyed cast steel grades according to DIN 1681, the materials of this group show distinctly higher values of the notch impact energy. As a result of their low carbon content (0.23 per cent maximum), they are well suitable for welding.PropertiesGeneralPropertyTemperatureValueC

The steel is used for the manufacture of bolts, nuts and rivets (and similar shaped parts).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 G

The steel is used for the manufacture of bolts, nuts and rivets (and similar shaped parts).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 G

The steel is suitable for cold heading and is used for the manufacture of bolts, nuts and rivets (and similar shaped parts).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C19

The steel is suitable for cold heading and is used for the manufacture of bolts, nuts and rivets (and similar shaped parts).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C19

The steel is used for the manufacture of bolts, nuts and rivets (and similar shaped parts).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 G

Seamless precision steel tube made from St 35 is mainly used as construction element with special requirements in dimension accuracy, small wall thicknesses and good surface condition. The tubes are made in different grades (A and C). Grade C is valid for conduits. Grade A: for mechanical load witho