CuZn5 (CW500L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. CuZn5 has a favorable conductivity, resistance to atmospheric corrosion and is ideal for enamelling. Processing properties: warm forming: moderately cold forming: good machinab

CuZn5 (CW500L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. CuZn5 has a favorable conductivity, resistance to atmospheric corrosion and is ideal for enamelling. Processing properties: warm forming: moderately cold forming: good machinab

CuZn5 (CW500L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. CuZn5 has a favorable conductivity, resistance to atmospheric corrosion and is ideal for enamelling. Processing properties: warm forming: moderately cold forming: good machinab

Cold-rolled narrow strip made of the mild steel C60E will be delivered in thicknesses up to 6 mm for quenching and tempering and for quenched and tempered cold strip in thicknesses between 0.3 mm and 3.0 mm in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), -

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelDimensionPropertyValueWall thickness1 - 8 mmMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C16 - 25 %Hardness, Rockwell

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelDimensionPropertyValueWall thickness1 - 8 mmMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C26 - 35 %Hardness, Rockwell

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelDimensionPropertyValueWall thickness1 - 8 mmMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C11 - 25 %Elongation A5, tra

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelDimensionPropertyValueWall thickness1 - 8 mmMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C8 - 23 %Elongation A5, tran

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C36 - 43 %Hardness, Rockwell B23.0 °C85 [-]Hardness, Vickers23.0 °C170 [

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C34 - 41 %Hardness, Rockwell B23.0 °C85 [-]Hardness, Vickers23.0 °C170 [

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C32 - 39 %Hardness, Rockwell B23.0 °C74 - 89 [-]Hardness, Vickers23.0 °C

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C12 - 14 %Elongation A8023.0 °C12 %Poisson's ratio23.0 °C0.29 [-]Ty

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C36 - 43 %Hardness, Rockwell B23.0 °C50 - 71 [-]Hardness, Vickers23.0 °C

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C13 - 15 %Elongation A8023.0 °C12 %Poisson's ratio23.0 °C0.29 [-]Ty

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C15 - 17 %Elongation A8023.0 °C14 %Poisson's ratio23.0 °C0.29 [-]Ty

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C36 - 43 %Hardness, Rockwell B23.0 °C65 - 80 [-]Hardness, Vickers23.0 °C

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C36 - 43 %Hardness, Rockwell B23.0 °C74 - 89 [-]Hardness, Vickers23.0 °C

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C34 - 41 %Hardness, Rockwell B23.0 °C50 - 71 [-]Hardness, Vickers23.0 °C

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C34 - 41 %Hardness, Rockwell B23.0 °C65 - 80 [-]Hardness, Vickers23.0 °C

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C34 - 41 %Hardness, Rockwell B23.0 °C74 - 89 [-]Hardness, Vickers23.0 °C