JIS 6061 is a readily available alloy that has good surface finish and ability to be anodized.Easy of weldability and brazability with nice surface finish. Resistance to corrosion from seawater and atmospheric conditions. Suitable for hot forging.Quantity: 1 PCSPropertiesGeneralPropertyValueCommentD

Aluminum JIS 5052 is a non-heat treatable alloy with excellent finishing qualities. JIS 5052 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the

Aluminum JIS 6063 is an architectural alloy that offers users a high resistance to corrosion and excellent finishing characteristics. Easy to extrude with fair machinability, JIS 6063 can be both hot and cold formed and is commonly available as T6 temper as well as T4 temper.PropertiesGeneralPropert

Aluminum JIS 6063 is an architectural alloy that offers users a high resistance to corrosion and excellent finishing characteristics. Easy to extrude with fair machinability, JIS 6063 can be both hot and cold formed and is commonly available as T6 temper as well as T4 temper.PropertiesGeneralPropert

X5CrNi18-10 as a standard type of the CrNi-steels is comparable to X 5 CrNi 18 10 acc. to DIN 17440 : 1985-07. It shows high corrosion resistance but no resistance to intercrystalline corrosion in sensitized condition. It is resistant in delivery condition. The steel is well processable, suitable fo

Material X14CrMoS17, comparable to X 12 CrMoS 17 acc. to DIN 17440 : 1985-07 is a stainless free cutting steel. Application in tempered condition as construction parts for machine processing, such as screws, nuts, fittings, axles, bolts, spindles in water, steam and alkalescent and neutral media as

Boron-alloyed tempering steel for general machine engineering.The steel is shearable in the non treated condition.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Medium Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTy

The steel is used for rail vehicle engineering acc. to the selected standard DIN 5512-1.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.84 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa5

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0 °C164 GPaElongation20.0 °C28 %Poisson's ratio20.0 °C0.28 [-]She

High temperature steel for application in the pressure vessel and steam boiler manufacturing as well as nuclear power plant engineering.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.93 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C206 GPa20.0 °C196 - 198 GPa100.0 °

Properties: - stainless free cutting steel - application in quenched and tempered state - corrosion resistance is similar to an 13%-Cr-steel, because of its sulfur additional - application temperature: -25 to 550 °C Application: - for application enviroment like water, steam, weak alkaline and neutr

Welding GradePropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Medium Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Medium Carbon SteelElongation23.0 °C24 %Hardness, HBW23.0 °C131 - 187 [-]Poisson's rat

G-X 2 NiCrMoCuN 25 20, for components of pumps and apparatuses for the viscose producing industry, service temperatures up to 350 °CPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.9 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C195 GPaTypical for Austenitic Stainless S

Properties: - ferritic steel with small tendency to solidificate - tends heat treatment wiht following cold forming strongly to the coarse grain formation - corrosion resistant in oxidising and sour media, insensitively to crack corrosion - due to the good magnetic characteristics also for magnetic

- stainless steel with estra low carbon content - for special applications in automobile industry, electro industry and homeware industryPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.7 - 7.73 g/cm³MechanicalPropertyTemperatureValueElastic modulus20.0 °C217 - 220 GPa100.0 °C215 - 216 GPa20

Properties: - ferritic-austenitic - possesses small sensitivity to crack corrosion - exhibits better general corrosion resistance as 1.4362 - is better cutting machinably than austenites - high abrasion resistance and good runnability - high polishable - application temperature -60 to 350 °C Applica

- high strength stainless extra low carbon steel for special applications - corrosion resistance is similar to 1.4311PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.92 - 8 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C206 GPa20.0 °C196 - 198 GPa100.0 °C190 - 192 GPa2

Properties: - ferritc steel with better corrosion resistance than the general structure steels - lower costs as high-alloyed stainless steels - corrison resistance similar to the steels with 13 % Cr - not for stronger corrosion loadings - good resistance to abrasion - high static and dynamic strengt

S690G2QL is a fluid-tempered high strength weldable fine grained steel with a min. yield point of 690 N/mm². It is applicated for constructions whose behaviour predominantly depends on wear resistance of the material, e.g. wearing parts of mining and earth moving machines transport and crushing and

Malleable iron is a cast iron in which the graphite is present as temper carbon nodules, instead of flakes as gray iron or spherulites as in ductile iron. M8501 is high strength and/or wear resistance.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.2 - 7.34 g/cm³Typical for Malleable