X45CrSi9-3 is a martensitic Cr-Si-alloyed valve steel. The steel shows excellent nitriding and surface hardenability, it is suitable for upsetting. Moderate resistance in exhaust condensate. This applies also to lead compounds at increased temperatures. Tempering resistance at continuous operation u

X40CrSiMo10-2 is a martensitic CrSiMo-alloyed valve steel with high thermal resistance.Use: exhaust-valves (low scaling)PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.7 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C210 GPaElongation20.0 °C14 %Hardness, Brinell20.0 °C2

X33CrNiMnN23-8 is a Cr-Ni-Mn-W-N- alloyed valve steel.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C205 GPaElongation20.0 °C20 %Hardness, Rockwell C20.0 °C25 [-]Poisson's ratio23.0 °C0.3 [-]Typical for Austenitic S

EN-GJS-800-2 (before GGG-80 acc. to DIN 1693/01-73), a pearlitic cast iron with nodular graphite for cast parts of high strength and hardness, e.g. cutter heads, pinions, cast parts of high abrasion load, e.g. rabbles, worm wheel segments for construction machines. This cast iron mark applies to spe

Material CuSn3Zn9, mat. No. CW454K, is predominantly used in electrical engineering. The multicomponent alloy is characterized by a considerably lower stress corrosion sensitivity compared to the copper-zinc-alloys. The spring properties come up to alloy CuSn4 (CW450K). For the electrolytically tinn

Steel C60R is suitable for high loaded parts in vehicle, engine and machine engineering with enhanced workability at constant strength qualities (e.g. gear wheels, pinions, shafts). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in

Steel C60R is suitable for high loaded parts in vehicle, engine and machine engineering with enhanced workability at constant strength qualities (e.g. gear wheels, pinions, shafts). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in

Steel C60R is suitable for high loaded parts in vehicle, engine and machine engineering with enhanced workability at constant strength qualities (e.g. gear wheels, pinions, shafts). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in

Steel C60E is suitable for larger parts (heavy forged parts) of high load in vehicle, engine and machine engineering. Surface hardenable (e.g. crankshafts, bolts, transmission parts). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, i

Steel C50R is suitable for parts in vehicle, engine and machine engineering that require enhanced workability at constant strength qualities (e.g. transmission shafts, gear wheels). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in

Steel C50E is suitable for larger parts (heavy forged parts) in vehicle, engine and machine engineering (e.g. transmission parts, shafts, wheel hubs). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN

Steel C45R is suitable for mean loaded parts in vehicle, engine and machine engineering with enhanced workability at constant mechanical qualities (e.g. transmission shafts, gear wheels, clutch parts, bolts). Lowest application temperature -25°C. As a bright steel product it is used in the form of

Steel C45E is suitable for parts of mean load and higher dimension (heavy forged parts) and complexer form in vehicle and machine engineering (shipshafts, transmission parts, wheel hubs). Lowest application temperature -25°C, favorable creep behaviuor up to 480°C.. As a bright steel product it is u

Steel C40R is suitable for slightly higher loaded parts in vehicle, engine and machine engineering with enhanced workability at constant mechanical qualities (e.g. transmission parts, crank shafts, cylinder). Lowest application temperature -25°C. As a bright steel product it is used in the form of

Steel C40E is suitable for heat-resistant screws and larger forged parts as well as for parts of complexer form (e.g. gear wheels, camshafts) in vehicle and machine engineering. Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in vario

Steel C35R is suitable for slightly higher loaded parts in vehicle, engine and machine engineering with enhanced workability at constant mechanical properties (e.g. transmission parts, crank shafts, cylinder). Lowest application temperature -25°C. As a bright steel product it is used in the form of

Steel C35E is suitable for slightly higher loaded parts in vehicle and machine engineering that have higher dimension (large forged parts) and complexer forms as well as higher demands to constancy of qualities and surface appearance (e.g. transmission parts, crankshafts). Lowest application tempera

Steel 51CrV4 is suitable for high loaded parts in aircraft, vehicle, engine and machine engineering that require increased tempering resistance at best core qualities and high wear resistance (e.g.transmission and joint parts, axles). Furthermore application as spring and tool steel. Lowest applicat

Steel 41CrS4 is suitable for mean loaded parts in vehicle, engine and machine engineering with mean heat-treatment sections and enhanced workability. (e.g. gear wheels, transmission shafts, axles). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, brigh

Steel 41CrS4 is suitable for mean loaded parts in vehicle, engine and machine engineering with mean heat-treatment sections and enhanced workability. (e.g. gear wheels, transmission shafts, axles). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, brigh