CuZn15 (CW502L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn10. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderately cold forming: go

Highly creep resistant steel used for the production of pressure vessels and steam boilers and in the construction of nuclear power stations.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.9 - 7.93 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C206 GPa20.0 °C196 - 200

CuZn10 (CW501L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal conductivity is lower than for CuZn5. Favorable electrical conductivity. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderatel

CuSn6, mat. No. CW425K, is comparable to the DIN-make CuSn6, mat. No. 2.1020, acc. to DIN 17662 : 1983-12. Properties of the CuSn-alloy are predominantly determined by the tin-content. Tensile strength, yield point and hardness increase according to the rising cold forming grade, elongation after fr

Wire fom copper alloy for general purposes.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.5 - 8.55 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C114 GPa100.0 °C112 GPa200.0 °C107 GPa300.0 °C103 GPa400.0 °C96 GPa500.0 °C88 GPa600.0 °C77 GPa700.0 °C67 GPaElongation20.0

Tubes made from cryogenic alloyed high-grade steel X12Ni5 are predominantly used in apparatus, tank, line construction as well as in general machine and equipment engineering. Weldability is available.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.86 g/cm³27.0 °C7.82 g/cm³MechanicalPropert

Wire fom copper alloy for general purposes.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.67 - 8.7 g/cm³MechanicalPropertyTemperatureValueElastic modulus20.0 °C119 GPa100.0 °C116 GPa200.0 °C111 GPa300.0 °C106 GPa400.0 °C100 GPa500.0 °C91 GPa600.0 °C81 GPa700.0 °C71 GPaElongation20.0 °C45 %

Tubes made from cryogenic alloyed high-grade steel 12Ni14 are predominantly used in apparatus, tank, line construction as well as in general machine and equipment engineering. Weldability is available.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³27.0 °C7.86 g/cm³MechanicalPropert

CuNi2Si, mat. No CW111C, is counted among hardenable, low alloyed copper alloys. To the comparable make CuBNi2Si, mat. No 2.0855, acc. to DIN 17666 : 1983-12 applies: The material shows favorable electrical and thermal conductivity, corrosion resistance, high fatigue and creep resistance as well as

CuNi2Si, mat. No CW111C, is counted among hardenable, low alloyed copper alloys. To the comparable make CuBNi2Si, mat. No 2.0855, acc. to DIN 17666 : 1983-12 applies: The material shows favorable electrical and thermal conductivity, corrosion resistance, high fatigue and creep resistance as well as

Wire fom copper alloy for general purposes.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.73 - 8.8 g/cm³MechanicalPropertyTemperatureValueElastic modulus20.0 °C122 GPa100.0 °C119 GPa200.0 °C114 GPa300.0 °C109 GPa400.0 °C103 GPa500.0 °C94 GPa600.0 °C84 GPa700.0 °C74 GPaElongation20.0 °C22 %

CuNi2Si, mat. No CW111C, is counted among hardenable, low alloyed copper alloys. To the comparable make CuBNi2Si, mat. No 2.0855, acc. to DIN 17666 : 1983-12 applies: The material shows favorable electrical and thermal conductivity, corrosion resistance, high fatigue and creep resistance as well as

Steel P460NH is a high-temperature weldable alloyed high-grade steel for pressure vessel construction. Application temperature: approx. 400 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.84 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0

Seamless steel tube for pressure purposes with specified elevated temperature properties.The steel grade meet the essential requirements of Directive 97/23/EC.,Seamless tubes of the high-temperature X11CrMo9-1+I are used in steam boiler and pipeline construction, pressure vessel and apparatus engine

Seamless tubes of the high-temperature X10CrMoVNb9-1 are used in steam boiler and pipeline construction, pressure vessel and apparatus engineering, especially in chemical industry and power station construction at temperatures from approx. 200 °C to maximum 400 °C and simultaneously high pressures.

Material CuZn36Pb3, mat. No. CW603N, is an unhardenable wrought alloy. to the comparable make CuZn36Pb3, mat. No. 2.0375 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded

Material CuZn36Pb3, mat. No. CW603N, is an unhardenable wrought alloy. to the comparable make CuZn36Pb3, mat. No. 2.0375 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded

Material CuZn39Pb3, mat. No. CW614N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb3, mat. No. 2.0401 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for unleaded bras

Material CuZn39Pb2, mat. No. CW612N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb2, mat. No. 2.0380 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded

Steel C 45 is suitable for mean strained parts in vehicle manufacturing, engine and machine engineering (e.g. transmission shafts, gear wheels, transmission parts). Lowest application temp. -25 °C, favorable creep behaviour up to 480 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 - 7.