The steel 17 CrNiMo 6 is used for high loaded parts in the vehicle and mechanical engineering with high demands on toughness and core strength (e.g. gear parts, drive pinions). The lowest application amounts to -60 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 - 7.85 g/cm³MechanicalP

The steel 17 Cr 3 is used for high wear loaded smaller parts in the vehicle and mechanical engineering (e.g. camshafts, piston pins, cylinder). The lowest application amounts to -25 °C, the best application up to 25 mm nominal size.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.82 - 7.85 g

The steel 16 MnCrS 5 is used for larger parts with higher core strength and better machinability in the vehicle and mechanical engineering (e.g. gears, shafts, steering parts). The lowest application amounts to -25 °C, the best application up to 50 mm nominal size.PropertiesGeneralPropertyTemperatur

The steel 16 MnCr 5 is used for larger parts with higher core strength and advantageous toughness properties in the vehicle and mechanical engineering (e.g. gears, shafts, steering parts). The lowest application amounts to -25 °C, the best application up to 50 mm nominal size.PropertiesGeneralProper

The steel 15 CrNi 6 is used for parts in the vehicle and mechanical engineering with medium strength and high toughness (e.g. gears, shafts). The lowest application amounts to -60 °C, the best application up to 100 mm nominal size.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.84 - 7.85 g/

The steel is used for rail vehicle engineering acc. to the selected standard DIN 5512-3.The corresponding properties of EN 10088 shall be taken.Application example: railcar bodyRemarks: Protective coating is well applicable and necessary under increased corrosion load and for decorative purposes. No

The cast material G-NiCu30Nb shows very good resistance to sea water and possesses good corrosion properties against non-oxidizing inorganic acids, especially against sulphuric, hydrofluoric and phosphorous acid, against most organic acids and against alkaline solutions. Furthermore, the material is

G-X 40 SiCr 29, because of its relatively high resistance of scaling basically applicaple for burn drums, flame jets and flame pot, flame rood, annealing retorts. Furthermore for agitation arms and agitation sprockets, chute and protecting ring segments, hot plates, inset boxes, annealing snail, cru

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C2.7 g/cm³Typical for Wrought 6000 Series AluminiumMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C70 GPaTypical for Wrought 6000 Series AluminiumPlane-Strain Fracture Toughnes23.0 °C22 - 35 MPa·√mTypical for Wrought 6000 Se

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C2.7 g/cm³Typical for Wrought 1000 Series AluminiumMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C68 - 70 GPaTypical for Wrought 1000 Series AluminiumPlane-Strain Fracture Toughnes23.0 °C22 - 35 MPa·√mTypical for Wrought 10

DIN 1725-2 standard is replaced with EN 1706PropertiesGeneralPropertyValueCommentDensity2.65 - 2.7 g/cm³Typical for Cast 3xx.x Series AluminiumMechanicalPropertyValueConditionRelated StandardsCommentElastic modulus73.0 - 80.0 GPaTypical for Cast 3xx.x Series AluminiumElongation2.0 - 4.0 %T6DIN 1725-

Properties: - high hardenable and wear resistant steel - because of its high carbon content, corrosion resistance ist similar to 13%-Cr-steels, although chromium content is high Application: - especially for small bearings, for cutting tools (knifes and srugival instruments) - for valve pins and noz

S690G3QL is a fluid-tempered high strength weldable fine grained steel with a min. yield point of 690 N/mm². It is applicated for constructions whose behaviour predominantly depends on wear resistance of the material, e.g. wearing parts of mining and earth moving machines transport and crushing and

S890G1QL is a fluid-tempered high strength weldable fine grained steel with a min. yield point of 890 N/mm². It is applicated for constructions whose behaviour predominantly depends on wear resistance of the material, e.g. wearing parts of mining and earth moving machines transport and crushing and

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelPoisson's ratio23.0 °C0.29 [-]Typical for Low Carbon SteelShear modulus23.0 °C82 GPaTy

G-X 160 CrSi 18, especially for wear and abrasion loaded cast pieces, like pipe rods, agitation sprocket, caps etc. resistance: - in carborising gas: mittel - in nitrogenous gas: low - in oxidising sulfureous gas: vers good - in reductive sulfureous gas: good to middle - temperature loading on air:

G-X 40 CrNi 27 4, for wear and corrosion resistant casting components for the chemical industry, ship building, mining, like valve-casings, press spindles, fly cutters.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.7 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C195 G

Reactor grade unalloyed niobium sheet, strip and plate.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.57 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C103 GPaElongation A2520.0 °C15 - 20 %Poisson's ratio23.0 °C0.4 [-]Typical for NiobiumShear modulus23.0 °C38 GPaT

Commercial grade niobium-zirconium alloy bar, rod and wire.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.57 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C103 GPaElongation20.0 °C15 - 20 %Poisson's ratio23.0 °C0.4 [-]Typical for NiobiumShear modulus23.0 °C38 GPaT

Reactor grade niobium-zirconium alloy bar, rod and wire.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.57 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C103 GPaElongation20.0 °C15 - 20 %Poisson's ratio23.0 °C0.4 [-]Typical for NiobiumShear modulus23.0 °C38 GPaTypi