Commercial grade unalloyed niobium bar, rod and wire.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.57 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C103 GPaElongation20.0 °C20 - 25 %Poisson's ratio23.0 °C0.4 [-]Typical for NiobiumShear modulus23.0 °C38 GPaTypical

Reactor grade unalloyed niobium bar, rod and wire.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.57 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C103 GPaElongation20.0 °C20 - 25 %Poisson's ratio23.0 °C0.4 [-]Typical for NiobiumShear modulus23.0 °C38 GPaTypical fo

DIN Ti4 titanium is the strongest of the four commercially unalloyed titanium grades. It is as well known for its good formability, weldability and ductility and its excellent corrosion resistance.Quantity: € 250Additional services: Project business and tailor made products; material consultancyOERL

DIN Ti4 titanium is the strongest of the four commercially unalloyed titanium grades. It is as well known for its good formability, weldability and ductility and its excellent corrosion resistance.Quantity: € 250Additional services: Project business and tailor made products; material consultancyOERL

DIN Ti3 titanium is the third of four commercially unalloyed titanium grades. It is known for its high strength and good corrosion resistance. It also has good impact properties at low temperature and is suitable for being welded, machined, cold worked and cast. PropertiesGeneralPropertyTemperatureV

DIN Ti3 titanium is the third of four commercially unalloyed titanium grades. It is known for its high strength and good corrosion resistance. It also has good impact properties at low temperature and is suitable for being welded, machined, cold worked and cast. PropertiesGeneralPropertyTemperatureV

DIN Ti2Pd has physical and mechanical properties equivalent to CP3 titanium or Grade 2. It has excellent welding and fabrication properties and is extremely resistant to corrosion especially from reducing acids.PropertiesGeneralPropertyTemperatureValueConditionRelated StandardsShapeDensity20.0 °C4.5

DIN Ti2 titanium is the second of four commercially unalloyed titanium grades. It has a moderate strength as well as excellent welding properties. The material is known for its good resistance to oxidation and corrosion.Quantity: 300 EURAdditional services: Project based stainless steel packages for

DIN Ti2 titanium is the second of four commercially unalloyed titanium grades. It has a moderate strength as well as excellent welding properties. The material is known for its good resistance to oxidation and corrosion.Quantity: 300 EURAdditional services: Project based stainless steel packages for

DIN Ti1Pd is highly resistant to corrosion has similar physical and mechanical properties to Titanium CP Grade 2.PropertiesGeneralPropertyTemperatureValueConditionRelated StandardsShapeDensity20.0 °C4.505 g/cm³WeldedDIN 17851, VdTÜV WB 230-2, VdTÜV WB 230-1, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN

DIN Ti1 titanium is the first of four commercially pure titanium grades. DIN Ti1 is considered the softest titanium with the highest ductility. This grade is known for its good cold forming characteristics and high impact toughness. It also provides excellent corrosion resistance and welding propert

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelPoisson's ratio23.0 °C0.29 [-]Typical for Low Carbon SteelShear modulus23.0 °C82 GPaTy

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A5023.0 °C20 %Poisson's ratio23.0 °C0.29 [-]Typical for Low Carbon SteelShe

Material X2CrNiN18-7 is comparable to X 2 CrNiN 18 7 acc. to SEW 400 :1991-02. This material is a high-strength stainless ELC-steel for special applications. Its corrosion resistance is comparable to 1.4311. It shows resistance to intercrystalline corrosion also in sensitized condition.PropertiesGen

21MnCr5 is a case hardened steel. It achieves surface hardnesses of approx. 60 HRC in carburized condition. Application when required high surface hardness and ductile core. It is suitable for die typing and burnishing. Application: small and medium forms for processing of thermo and and thermosett

Material X105CrMo17 is comparable to X 105 CrMo 17 acc. to SEW 400 :1991-02. The material is a high hardenable and wear resistant steel. It is particularly suitable for small ball bearings, for cutting tools, such as butchers knives, scalpels, for valve needles and spray nozzles. Despite the higher

Steel 20NiCrMo2-2 is suitable for parts in vehicle manufacturing and machine engineering, which are wear loaded at mean core strength, high ductility and fatigue strength (e.g. gear wheels, shafts, axles).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.84 - 7.85 g/cm³MechanicalPropertyTempe

Gold-based solder alloy. Soft solders are characterized by a liquidus temperature <450°C. High precious metal-containing special soft solders are always used when the properties of the classic SnPb soft solders do not meet the desired requirements. This is the case in different areas of electronics

The gold-silver-copper material AuAg20Cu10, also Au70Ag20Cu10, 70Au20Ag10Cu, exhibits sufficient corrosion behavior as well as satisfactory wear behavior and is used as contact material (monolithic contact spring material) for tapping contacts as well as potentiometer alloy. It is ductile, corrosion

Silver-based vacuum braze alloy AgPd5, also Ag95Pd5 or 95Ag5Pd is used in connection technology metallized ceramics / metal in tube construction as well as in vacuum apparatus construction.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C10.5 g/cm³MechanicalPropertyTemperatureValueCommentElast