PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.81 g/cm³T6AA Standards, ASTM B247MechanicalPropertyValueConditionRelated StandardsCommentBending Fatigue Strength125.0 MPaT6AA StandardsElastic modulus72.0 GPaT6AA Standards, ASTM B247Hardness, Brinell110.0 [-]T6AA StandardsPlane-Strai

Low-alloy titanium for seamless pipes for pressure equipment requiring monitoring acc. to AD 2000 W0, directive 2014/68/EU and for nuclear engineering.PropertiesGeneralPropertyTemperatureValueConditionRelated StandardsShapeDensity20.0 °C4.505 g/cm³AnnealedDIN 17850, VdTÜV WB 230-3, DIN 17851, VdTÜV

The corrosion resistant rolled steel X 1 CrNi 25 21 (new designation: X1CrNi25-21), material number 1.4335 is applicable acc. to VdTÜV-material specification 468 : 2001for pressure vessels as per TRB 100 and AD-data sheets W 2 and W 10 from -196 to 400 °C. Application: in nuclear power engineering a

The steel is used for rail vehicle engineering acc. to the selected standard DIN 5512-1.The corresponding properties of EN 10025-2 shall be taken.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C210 GPa100.0 °C205 GPa200.

The steel is used for rail vehicle engineering acc. to the selected standard DIN 5512-1.The corresponding properties of EN 10025-2 shall be taken.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic

DIN 3.3211 is a readily available alloy that has good surface finish and ability to be anodized.Easy of weldability and brazability with nice surface finish. Resistance to corrosion from seawater and atmospheric conditions. Suitable for hot forging.PropertiesGeneralPropertyTemperatureValueConditionR

The material AlMgSiPb is a free-cutting alloy (boring and turning quality). It is warm and cold hardenable. Breaking the splinter is caused by the additive of Pb, and thus a troublefree splinter removal is possible with relatively high cutting performance. From the standardised free-cutting steel al

The alloy AlCu2,5Mg0,5 (see also AlCu2,5Mg0,5, material number 3.1124, Werkstoffleistungsblätter der Deutschen Luftfahrt WL 3.1124, part of 1 and part of 100, Ausgn. 12.87) belongs to the type of alloy Al-Cu-Mg, which found of the aluminum wrought machine materials as first in the technology use. Al

Steel X20CrMo13 shows increased thermal and corrosion resistance. Application in tempered condition at operating temperatures from 450 to 500 °C. for turbine blades, valve cones, valve seats in hot steam valves. The steel is suitable for mirror finishing. X20CrMo13 shows owing to the Mo-content high

Steel C22E is suitable for low strained components of higher dimensions (heavy forged parts) and more complex forms as well as higher demands on uniformity of qualities and surface appearance in vehicle and machine engineering (e.g. transmission parts, crankshafts).PropertiesGeneralPropertyTemperatu

Steel C45E is applicable for medium loaded parts of higher dimensions (large forged parts) and more complex form in vehicle manufacturing and machine engineering (e.g. shipshafts, transmission parts, wheel hubs).PropertiesGeneralPropertyTemperatureValueConditionRelated StandardsShapeDensity20 °C7.8

Cold-rolled narrow strip made of the mild steel C22E will be delivered in thicknesses up to 6 mm for quenching and tempering in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), - cold rolled (+CR). The delivery condition annealed to globular carbides (+AC) can

Cold-rolled narrow strip made of the mild steel C10E will be delivered in thicknesses up to 10 mm for case hardening in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), - cold rolled (+CR).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³Mechani

= 99,9% and a high residual copper-content. Tensile strength and Brinell hardness are increasable by cold forming. SF-Cu (Cu-DHP) is hydrogen resistant and shows the lowest thermal and electrical conductivity of the pure copper materials. Processing properties: hot forming: very good cold forming:

The steel P295GH is a high temperature steel. Application: steam boiler and pressure vessel engineering, collectors, distributors, welding-neck laps, flanges and other shaped pieces. Maximum temperature of use: 530 °C, also in nuclear power station construction.PropertiesGeneralPropertyTemperatureVa

The steel P250GH is a high temperature steel for boiler engineering. Application: use for shaped pieces and flanges.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300

The steel P235GH is a high temperature steel for boiler engineering. Application: use in steam boiler and pressure vessel engineering.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa

Steel grade X6CrNiTi18-10 acc. to DIN EN 10272 : 2001-01is used for hot and cold formed rods for pressure vessels. the material is the stabilized by Ti option of 1.4301 (X5CrNi18-10). The steel is therefore resistant to intercrystalline corrosion also on sensitized condition. The steel is unsuitable

The alloy AlMn1 is an Al-Mn alloy, which belongs to the nature-hard aluminum materials. Mn increases the strength compared with pure aluminium, but it does not impair the corrosion resistance. The alloy belongs to the nature-hard aluminum materials. A strength increase can only occur by cold forming

The alloy AlMn0,5Mg0,5 is special one for the packing planned alloy. The alloy belongs to the nature-hard aluminum materials. A strength increase can only occur by cold forming. It is very well warm and cold formable and is very well suitable to the deep-drawing (no lappet formation). Because of the