S235JRG1 is applicable for welding constructions at temperatures of -20°C subject to the load. Max product thickness accounts for 25 mm. The steel shows for higher sections a cleavage fracture sensitivity. For this steel are available (mat. No 1.0121 acc. to DIN EN 10025) grades for: - folding (KQ)-

The steel C 10 is used for wear loaded parts with low core strength in the vehicle and mechanical engineering (e.g. pins, lever, compression mouldings and stampings). The lowest application amounts to -25 °C, the best application from 5 to 10 mm nominal size. As bright steel product it is used in th

The material X12Cr13, mat. no. 1.4006, is used for rods (for pressure vessels), forgings and drawn wire acc. DIN 17440 : 1996-09. For the application acc. DIN 17440 : 1985-07 (X 6 Cr 13) resp. acc. DIN EN 10088-1,-2,-3 : 1995-08 (X6Cr13) applies: Application as construction parts in water and steam

High temperature tube steel for welded tubes and tube products. Applicable up to 500 °C wall temperature for continuous operation. Application: vessel construction, apparatus construction, petrochemical industryPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemper

High temperature tube steel for welded tubes and tube products. Applicable up to 500 °C wall temperature for continuous operation. Application: vessel construction, apparatus construction, petrochemical industryPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemper

High temperature steel for high pressure hydrogenation vessels. It is scale resistant up to 650 °C as well as chemical resistant to aggressive (e.g. sulphurous) oils. Application: hydration facilities and petroleum distillation facilities for tubes and shapes, in the quenched and tempered condition

High temperature tube steel for seamless tubes. Applicable up to 500 °C wall temperature for continuous operation. Application: steam vessel and pressure vessel construction, apparatus construction, petrochemical industryPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³50.0 °C7.84 g/

The steel StE 360.7 TM is produced as welded tube in the conditions thermomechanical treated. Tubes of this steel are conform acc. 5L, 5LX and 5LS of the American Petroleum Institute (API). The Attention should be paid to the technical regulation for combustible liquids TRbF 301. Application: pipe

The steel StE 360.7 is produced as seamless or welded tube in the conditions untreated or normalised. Tubes of this steel are conform acc. 5L, 5LX and 5LS of the American Petroleum Institute (API). The Attention should be paid to the technical regulation for combustible liquids TRbF 301. Applicati

The steel StE 320.7 TM is produced as welded tube in the conditions thermomechanical treated. Tubes of this steel are conform acc. 5L, 5LX and 5LS of the American Petroleum Institute (API). The Attention should be paid to the technical regulation for combustible liquids TRbF 301. Application: pipe

The steel StE 320.7 is produced as seamless or welded tube in the conditions untreated or normalised. Tubes of this steel are conform acc. 5L, 5LX and 5LS of the American Petroleum Institute (API). The Attention should be paid to the technical regulation for combustible liquids TRbF 301. Applicati

The steel StE 290.7 TM is produced as welded tube in the conditions thermomechanical treated. Tubes of this steel are conform acc. 5L, 5LX and 5LS of the American Petroleum Institute (API). The Attention should be paid to the technical regulation for combustible liquids TRbF 301. Application: pipe

The steel StE 290.7 is produced as seamless or welded tube in the conditions untreated or normalised. Tubes of this steel are conform acc. 5L, 5LX and 5LS of the American Petroleum Institute (API). The Attention should be paid to the technical regulation for combustible liquids TRbF 301. Applicati

The steel StE 240.7 is produced as seamless or welded tube in the conditions untreated or normalised. Tubes of this steel are conform acc. 5L, 5LX and 5LS of the American Petroleum Institute (API). The Attention should be paid to the technical regulation for combustible liquids TRbF 301. Applicati

The steel StE 210.7 is produced as seamless or welded tube in the conditions untreated or normalised. Tubes of this steel are conform acc. 5L, 5LX and 5LS of the American Petroleum Institute (API). The Attention should be paid to the technical regulation for combustible liquids TRbF 301. Applicati

Steel Cm 22 is suitable for low strained parts in vehicle manufacturing and machine engineering that have to meet higher load capacity requirements while maintaining mechanical qualities ( transmission parts, crankshafts, cylinder). Lowest application temperature -25 °C.PropertiesGeneralPropertyTemp

Steel CK 22 is suitable for low strained parts in vehicle manufacturing and machine engineering with higher dimensions (heavy forged parts) and complexer forms as well as higher requirements to uniformity of qualities and surface appearance (e.g. transmission parts, crankshafts). Lowest application

Steel C 22 is suitable for low strained parts of small heat treatment sections in vehicle manufacturing and machine engineering (e.g. piston-rods, gear wheels). Lowest application temperature -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 g/cm³MechanicalPropertyTemperatureValueEl

Aluminum ASTM 6063 is an architectural alloy that offers users a high resistance to corrosion and excellent finishing characteristics. Easy to extrude with fair machinability, ASTM 6063 can be both hot and cold formed and is commonly available as T6 temper as well as T4 temper.PropertiesGeneralPrope

Steel C25E is suitable for low strained parts of higher dimension and more complex form as well as higher demands on uniformity of proprties and surface appearance (e.g. transmission parts, crankshafts). Lowest working temperature -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.82 -