Steel C 22 is suitable for low strained parts of small heat treatment sections in vehicle manufacturing and machine engineering (e.g. piston-rods, gear wheels). Lowest application temperature -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 - 7.85 g/cm³MechanicalPropertyTemperature

6 mm. Permitted for pressure vessel construction up to 300 °C, up to 550 °C subject to absence of intercrystalline attack causing media. Unsuited for mirror-polishing due to the Ti-addition. The material is approved in civil engineering for construction parts of carrying function. The sort is allowe

Tubes made from cryogenic unalloyed quality steel P265NL are predominantly used in apparatus, tank, line construction as well as in general machine and equipment engineering. Weldability is available.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon

Tubes made from cryogenic unalloyed quality steel P255QL are predominantly used in apparatus, tank, line construction as well as in general machine and equipment engineering. Weldability is available.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon

Tubes made from cryogenic unalloyed quality steel P215NL are predominantly used in apparatus, tank, line construction as well as in general machine and equipment engineering.Weldability is available.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon S

The basic type of the austenitic CrNi-steels X5CrNi18-10 shows high corrosion resistance but no resistance to intercrystalline corrosion in sensitized condition as well as favorable workability. The steel is suitable for mirror-polishing, is well cold formable, weldable and wear resistant. Applicati

The steel X2CrNiMoN17-13-3 is a fully austenitic mirror-polishable steel showing higher strength by N-alloying and higher corrosion resistance especially to unoxidizing and halogenated media than 1.4406 by higher Mo-addition. Higher resistance to selective attack than 1.4435, excellent fatigue stren

Cold rolled low carbon steel for flat products for vitreous enamelling (direct enamelling, as well as for special applications of conventional two coat enamelling for better sag resistance).Application: domestic appliances (cooking, laundry), sanitary ware (bathtubs, shower trays, sinks), architectu

Cold rolled low carbon steel for flat products for vitreous enamelling (direct enamelling, as well as for special applications of conventional two coat enamelling for better sag resistance).Application: domestic appliances (cooking, laundry), sanitary ware (bathtubs, shower trays, sinks), architectu

Steel L360NB is produced as seamless or welded pipe for flammable media in condition normalized or normalizing formed. Its yield stress is between 360 and 510 N/mm². The steel is weldable, its carbon equivalent CEV accounts for max. 0.42. To the welding seam (welding methods SAW, COW) applies a mand

Steel L369MB is produced as welded pipe for flammable media in condition thermomechanically rolled. Its yield stress is between 360 and 510 N/mm². The steel is weldable, its carbon equivalent CEV accounts for max. 0.41. To the welding seam (welding methods SAW, COW) applies a mandrel-diameter for th

Steel L290MB is produced as welded pipe for flammable media in condition thermomechanically rolled. Its yield stress is between 290 and 440 N/mm². The steel is weldable, its carbon equivalent CEV accounts for max. 0.40. To the welding seam (welding methods SAW, COW) applies a mandrel-diameter for th

The austenitic steel X2CrNiMo17-12-2, a modification of the steel 1.4401, is a steel of high resistance to unoxidizing acids and chloride-containing media. The material is mirror-polishable and well cold formable. Enhanced corrosion properties by lowered C-content compared to 1.4571. The material is

RSt 37-2 is used for for welded constructions stress dependent up to - 25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175

S275J2C is the cold forming grade of the S275J2. The steel is suited for bending and folding up to thicknesses of 30 mm and suited for roll forming up to 8 mm thickness (minimum values for the radius see Formability - Bending - Folding). Application: structural steel workPropertiesGeneralPropertyTe

S235J2C is the cold forming grade of the S235J2. The steel is suited for bending and folding up to thicknesses of 30 mm and suited for roll forming up to 8 mm thickness (minimum values for the radius see Formability - Bending - Folding). Application: structural steel workPropertiesGeneralPropertyTe

The steel Cm 15 is used for wear loaded parts with higher core strength in the vehicle and mechanical engineering (e.g. levers, joints, gears). Because of the S-content the steel has a better machinability. The lowest application amounts to -25 °C, the best application from 5 to 10 mm nominal size.P

The steel Ck 15 is used for increased wear loaded parts with higher core strength in the vehicle and mechanical engineering as well as for parts of larger dimension and complexer shape as the base grade C 15 (e.g. levers, joints, gears). The lowest application amounts to -25 °C.PropertiesGeneralProp

The steel Ck 10 is used for smaller wear loaded parts with low core strength in the vehicle and mechanical engineering as well as for parts of larger dimension and complexer shape as the base grade C 10 (e.g. pins, bushes, compression mouldings and stampings). The lowest application amounts to -25 °

Steel grade X6CrNiNb18-10 acc. to DIN EN 10272 : 2001-01is used for hot and cold formed rods for pressure vessels. The corrosion properties are comparable to 1.4541. The steel is resistant to intercrystalline corrosion also on sensitized condition, but it shows tendency to hot shortness under certai