G-X 40 CrNiSi 25 20, for parts of ovens with highest mechanical loadings, previously loaded to high heat resistance, like transport elements in oven for annealing, tempering, sheet normalising and throughput, this are for example rolls, bearing arbor, bearing grate, bolts, anchor, lever, oven plates

G-X 40 CrNiSi 25 12, especially applicable for units with high mechanical loading, like chain links and shaking chanel. resistance: - in oxidising burning atmosphere: 1100°C - in reductive burning atmosphere: 1040°C - in oxidising sulfureous gas: 1080°C - in reductive sulfureous gas: 750°CProperties

G-X 40 CrNiSi 22 9, applicable for parts of oven and burning constructions, like oven bars, transport grates, snail retorts, hot plates, annealing hood, saucer and caps, burning roods, annealing and hardening boxes and transport rollings. resistance: - in oxidising burning atmosphere: 950°C - in red

G-X 25 CrNiSi 20 14, for applications which demand high heat resistance in continuous duty, max. resistance at 1000°C resistance: - in oxidising burning atmosphere: 1000°C - in reductive burning atmosphere: 950°C - in oxidising sulfureous gas: 900°CPropertiesGeneralPropertyTemperatureValueDensity20.

G-X 25 CrNiSi 18 9, high heat resistance and insensitiveness against changing temperature. For parts of oven like dampers, transport chains, retorts, annealing and hardening boxes, traction clamps, bearing bottoms, bearing rods, hot gas ventilators. resistance: - in oxidising burning atmosphere: 850

Material GX5CrNiNb19-11 is equivalent to trademark G-X 5 CrNiNb 18 9 acc. to DIN17445-84. The material is used for cast parts, pressure vessels as well as in food, film, photo, color, soap, paper, textile and nitric acid industry, in explosive and viscose industry. GX5CrNiNb19-11 is ic-resistant and

G-X 22 CrNi 17, for blade wheels, rings for rudder bearings, sealing rings, cocks, valve guidancesPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.7 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C220 GPaTypical for Ferritic Stainless SteelElongation20.0 °C4 %Hardness, Br

Material GX5CrNiMo19-11-2 is equivalent to trademark G-X6 CrNiMo 18 10 acc. to DIN 17445-84. This material is used for fittings, pumps, agitators, filters and tanks in chemical industry, textile, viscose and cellulose industry. It is weldable without preheating. It is unsuitable for corrosion applic

Material GX5CrNi19-10 is eqivalent to trademark G-X 6 CrNi 18 9 acc. to DIN17445-84. The DIN-material is predominantly used for fittings and in machine engineering, e.g. for pumps, centrifuges, agitators as well as for parts in food, dairy, beverage and packaging industry. This material is weldable

G-X 8 CrNi 13, for cast parts, which are exposed to the air moisture, water and water steam, like blade wheels, blade wheel-buckets, components of pumps and valvesPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.7 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C220 GPaTyp

G-X 5 CrNi 13 4, for parts in the water power engineering, like water turbine casings and -guidances, for shipbuilding and building of compressores, cold-toughPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.7 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C220 GPaTypical

The fully killed machining steel 60 SPb 20 is used for mass parts of highest strength, especially for lower toughness demands cross-sectional. Its better machinable because of the Pb addition. Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).P

The fully killed machining steel 60 SPb 20 is used for mass parts of highest strength, especially for lower toughness demands cross-sectional. Its better machinable because of the Pb addition. Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).P

The fully killed machining steel 60 SPb 20 is used for mass parts of highest strength, especially for lower toughness demands cross-sectional. Its better machinable because of the Pb addition. Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).P

G-X 35 CrMo 17, for medical instruments, components of machines and armatures with increase resistance against low concentrated acids and chlorid containing media.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.7 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C220 GPaTyp

The fully killed machining steel 45 SPb 20 is used for mass parts of higher strength, especially for lower toughness demands cross-sectional. Its better machinable because of the Pb addition. Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).Pr

The fully killed machining steel 45 SPb 20 is used for mass parts of higher strength, especially for lower toughness demands cross-sectional. Its better machinable because of the Pb addition. Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).Pr

The fully killed machining steel 45 SPb 20 is used for mass parts of higher strength, especially for lower toughness demands cross-sectional. Its better machinable because of the Pb addition. Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).Pr

The fully killed machining steel 35 SPb 20 is used for mass parts of mean strength, especially for lower toughness demands cross-sectional. Its better machinable because of the Pb addition. Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).Prop

The steel C90S is used as cold rolled strip for springs and special applications in thicknesses of up to 6 mm and as tempered cold strip in thicknesses from 0.30 to 3.00 mm.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Medium Carbon SteelMechanicalPropertyT