The austenitic steel X1NiCrMoCu25-20-5 has a high resistance to highly aggressive organic and inorganic acids, high pitting corrosion and largely stress corrosion resistance. Its pitting index is with 39 the second best. The material is resistant to intercrystalline corrosion. Application: for tempe

The material X3CrNiMo17-13-3 has a similar corrosion resistance like 1.4401. It shows slightly improved resistance to selective corrosion due to the higher Mo-content. The material is in delivery condition resistant to intercrystalline corrosion. Application for acid resistant apparatus in chemical

The material X2CrNiMo17-12-2 is a modification of steel 1.4401 with high resistance to non oxidizing acids and chloride containing media. This steel is suitable for mirror finishing and very good cold formable. Its corrosion properties are still improved owing to the lowered C-content. The material

Seamless tubes made from St 52.0 are used in the apparatus engineering, container and pipe construction as well as mechanical engineering. The steel is weldable.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueElastic modulus-100.0 °C217 GPa20.0 °C210 - 212 GPa100.0 °C205 - 207 GPa200.0 °C195 - 199 GPa300.0 °C185 - 192 GPa400.0 °C175 - 184 GPa500.0 °C175 GPa600.0 °C164 GPaElongation20.0 °C20 - 22 %Elongation

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0 °C164 GPaElongation20.0 °C20 - 22 %Elongation, transverse20.0 °C18 -

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.82 - 7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C210 - 212 GPa100.0 °C205 - 207 GPa200.0 °C195 - 199 GPa300.0 °C185 - 192 GPa400.0 °C175 - 184 GPa500.0 °C175 GPa600.0 °C164 GPaElongation20.0 °C13 -

High temperature steel for high pressure hydrogenation vessels. It is scale resistant up to 650 °C as well as chemical resistant to aggressive (e.g. sulphurous) oils. Application: hydration facilities and petroleum distillation facilities for tubes and shapes, in the quenched and tempered condition

High temperature steel for high pressure hydrogenation vessels. It is scale resistant up to 650 °C as well as chemical resistant to aggressive (e.g. sulphurous) oils. Application: hydration facilities and petroleum distillation facilities for tubes and shapes, in the quenched and tempered condition

PropertiesGeneralPropertyValueConditionRelated StandardsShapeDensity2.69 g/cm³T7EN 573-3, EN 755Rod, TubeMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus70.0 GPaT7EN 573-3, EN 755Rod, TubeHardness, Brinell55.0 [-]T7EN 573-3, EN 755Rod, TubePlane-Strain Fracture Toughnes22

PropertiesGeneralPropertyValueCommentDensity2.65 - 2.7 g/cm³Typical for Wrought 5000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsCommentElastic modulus69.0 - 70.0 GPaTypical for Wrought 5000 Series AluminiumHardness, Brinell90.0 [-]H116AA StandardsPlane-Strain Fracture Toughnes2

PropertiesGeneralPropertyValueCommentDensity2.65 - 2.7 g/cm³Typical for Wrought 5000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsCommentElastic modulus69.0 - 70.0 GPaTypical for Wrought 5000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 5000

PropertiesGeneralPropertyValueCommentDensity2.65 - 2.7 g/cm³Typical for Wrought 5000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsCommentElastic modulus69.0 - 70.0 GPaTypical for Wrought 5000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 5000

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.69 g/cm³OAA Standards, ASTM B209MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus69.0 GPaOAA Standards, ASTM B209Hardness, Brinell32.0 [-]OAA StandardsPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wr

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.69 g/cm³H24AA StandardsMechanicalPropertyValueConditionRelated StandardsCommentElastic modulus69.0 GPaH24AA StandardsHardness, Brinell48.0 [-]H24AA StandardsPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 5000 Serie

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.66 g/cm³OAA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus71.0 GPaOAA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241Plane-Strain Fracture Toughnes22.0

PropertiesGeneralPropertyValueConditionRelated StandardsDensity2.66 g/cm³H24AA Standards, ASTM B209MechanicalPropertyValueConditionRelated StandardsCommentElastic modulus70.0 GPaH24AA Standards, ASTM B209Plane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought 5000 Series AluminiumPoisson

Material X6Cr17 is comparable to X 6 Cr 17 acc. to DIN 17440 : 1985-07. This material is a ferritic steel (17% Cr), largely resistant in water, steam, weak acids and bases, oxidizing acids (e.g. nitric acid). As a cold rolled sheet used for washing machines and kitchen parts, silverware, facings, tr

The material X3CrNiMo17-13-3 has a similar corrosion resistance like 1.4401. It shows slightly improved resistance to selective corrosion due to the higher Mo-content. The material is in delivery condition resistant to intercrystalline corrosion. Application for acid resistant apparatus in chemical

Propertties: - good corrosion resistance to water and steam - is able for high gloss polishing - application temperature: -40 up to 550°C Application: - for construction elements, requiring higher strengths because higher mechanical loadings - axis, parts for pumps, plunger, valve cone, nozzle pin,