Cold-rolled narrow strip made of the mild steel C55E will be delivered in thicknesses up to 6 mm for quenching and tempering and for quenched and tempered cold strip in thicknesses between 0.3 mm and 3.0 mm in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), -

Cold-rolled narrow strip made of the mild steel C50E will be delivered in thicknesses up to 6 mm for quenching and tempering and for quenched and tempered cold strip in thicknesses between 0.3 mm and 3.0 mm in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), -

Cold-rolled narrow strip made of the mild steel C50E will be delivered in thicknesses up to 6 mm for quenching and tempering and for quenched and tempered cold strip in thicknesses between 0.3 mm and 3.0 mm in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), -

Cold-rolled narrow strip made of the mild steel C45E will be delivered in thicknesses up to 6 mm for quenching and tempering in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), - cold rolled (+CR). The delivery condition annealed to globular carbides (+AC) can

Cold-rolled narrow strip made of the mild steel C45E will be delivered in thicknesses up to 6 mm for quenching and tempering in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), - cold rolled (+CR). The delivery condition annealed to globular carbides (+AC) can

Cold-rolled narrow strip made of the mild steel C40E will be delivered in thicknesses up to 6 mm for quenching and tempering in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), - cold rolled (+CR). The delivery condition annealed to globular carbides (+AC) can

Cold-rolled narrow strip made of the mild steel C40E will be delivered in thicknesses up to 6 mm for quenching and tempering in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), - cold rolled (+CR). The delivery condition annealed to globular carbides (+AC) can

CuZn37 (CW508L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn36. CuZn37 is the main alloy for cold forming. It shows favorable corrosion resistance to fresh water. Processing pr

CuZn37 (CW508L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn36. CuZn37 is the main alloy for cold forming. It shows favorable corrosion resistance to fresh water. Processing pr

CuZn37 (CW508L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn36. CuZn37 is the main alloy for cold forming. It shows favorable corrosion resistance to fresh water. Processing pr

CuZn37 (CW508L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn36. CuZn37 is the main alloy for cold forming. It shows favorable corrosion resistance to fresh water. Processing pr

Cold-rolled narrow strip made of the mild steel C35E will be delivered in thicknesses up to 6 mm for quenching and tempering in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), - cold rolled (+CR). The delivery condition annealed to globular carbides (+AC) can

Cold-rolled narrow strip made of the mild steel C30E will be delivered in thicknesses up to 6 mm for quenching and tempering in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC), - cold rolled (+CR). The delivery condition annealed to globular carbides (+AC) can

Material CuZn35Pb1, mat. No. CW600N, is an unhardenable wrought alloy. to the comparable make CuZn36Pb, mat. No. 2.0331 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded b

Cold-rolled narrow strip made of the alloy steel 25CrMo4 will be delivered in thicknesses up to 6 mm for quenching and tempering and for quenched and tempered cold strip in thicknesses between 0.3 mm and 3.0 mm in following conditions: - soft annealed or soft annealed and little rerolled (+A or +LC)

CuZn33 (CW506L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn30. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very goo

CuZn20 (CW503L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are worse than for CuZn15. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderately cold forming: go

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C7 - 10 %Poisson's ratio23.0 °C0.29 [-]Typical for Low Carbon Steel

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C7 - 10 %Poisson's ratio23.0 °C0.29 [-]Typical for Low Carbon Steel

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A523.0 °C7 - 10 %Poisson's ratio23.0 °C0.29 [-]Typical for Low Carbon Steel