The free cutting case hardening steel 38SMn28 shows an enhanced workability compared to 38SMn28. Application for turned parts of higher strength demands. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).PropertiesGeneralPr

The free cutting case hardening steel 38SMn28 is used for production of turned parts of higher strength demands. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).PropertiesGeneralPropertyTemperatureValueCommentDensity23.0

The free cutting case hardening steel 38SMn28 is used for production of turned parts of higher strength demands. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).PropertiesGeneralPropertyTemperatureValueCommentDensity23.0

The free cutting case hardening steel 38SMn28 is used for production of turned parts of higher strength demands. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).PropertiesGeneralPropertyTemperatureValueCommentDensity23.0

The free cutting case hardening steel 35SPb20 is used for bulk parts of mean strength, especially lower ductility demands in transversal direction compared to other C-steels (e.g. C35). Machinability enhancement is achieved by Pb-content. Application in car industry, apparatus, equipment and machine

The free cutting case hardening steel 35SPb20 is used for bulk parts of mean strength, especially lower ductility demands in transversal direction compared to other C-steels (e.g. C35). Machinability enhancement is achieved by Pb-content. Application in car industry, apparatus, equipment and machine

The free cutting case hardening steel 35SPb20 is used for bulk parts of mean strength, especially lower ductility demands in transversal direction compared to other C-steels (e.g. C35). Machinability enhancement is achieved by Pb-content. Application in car industry, apparatus, equipment and machine

The free cutting case hardening steel 35S20 is used for bulk parts of mean strength, especially if ductility demands in transversal direction are as high as for usual C-steels (e.g. C35). Cutting speed is increased but higher cracking risk according to rising C-content has to be considered. Applicat

E335GC is applicated as cold drawing grade. The steel is used for wear and strength loaded parts (bolts, shafts, spindles, axles, wedges). It is surface hardenable. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).Properti

E295GC is applicated as cold drawing grade. The steel is used for wear and strength loaded parts (bolts, shafts, spindles, wedges). As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).PropertiesGeneralPropertyTemperatureValue

Material CuZn30As (CW707R) is incomparable to a DIN-make. It is used for seamless circular tubes for heat-exchanger.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.55 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C100 - 125 GPaTypical for Wrought Copper BrassElongation2

The material according this standard is used for seamless, round tubes for heat exchangers, condensers, evaporators and desalination equipment.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.56 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-253.0 °C119 GPa-195.0 °C116 GPa-100

The material according this standard is used for seamless, round tubes for heat exchangers, condensers, evaporators and desalination equipment.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.56 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-253.0 °C119 GPa-195.0 °C116 GPa-100

CuZn28Sn1As (CW706R former identification: CuZn28Sn1) is an unhardenable copper alloy. High hardness and strength parameter are achievable by cold forming only. Tin increases corrosion resistance and improves sliding qualities. CuZn28Sn1As is dezincification resistant and resistant to river and indu

The material X17CrNi16-2, mat. no. 1.4057, is used acc. DIN 17440 : 1996-09 for rods (for pressure vessels), forgings and drawn wire. For the application acc. DIN 17440 : 1985-07 (X 20 CrNi 17 2) resp. acc. DIN EN 10088-1,-2,-3 : 1995-08 (X17CrNi16-2) applies: The quench and temperable grade (17 % C

The austenitic free-cutting steel X8CrNiS18-9, mat. no. 1.4305, is used for wire acc. DIN 17440 : 1996-09. The material is both in the delivery condition and in the welded condition not resistant to intercrystalline corrosion. According DIN 17440 : 1985-07 (X 10 CrNiS 18 9) resp. DIN EN 10088-1,-2,-

Material CuZn40Mn1Pb1AlFeSn (CW721R) is used in the form of rods, hollow rods, profiles, forging prematerial and forged parts.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.3 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C96 GPaHardness, Brinell20.0 °C140 - 190 [-]Hard

Material CuNi18Zn27, mat. No. CW410J is an alloy of high strength and hardness. To the comparabel mark CuNi18Zn27, mat. No. 2.0742, acc. to DIN 17663 : 1983-12 applies: Strength is further increasable due to the high strain hardening capability. The material does not embrittle at low temperatures.

Material CuNi18Zn27, mat. No. CW410J is an alloy of high strength and hardness. To the comparabel mark CuNi18Zn27, mat. No. 2.0742, acc. to DIN 17663 : 1983-12 applies: Strength is further increasable due to the high strain hardening capability. The material does not embrittle at low temperatures.

Steel C60R is suitable for high loaded parts in vehicle, engine and machine engineering with enhanced workability at constant strength qualities (e.g. gear wheels, pinions, shafts). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in