Steel C 60 is suitable for larger parts (heavy forged parts) and high load in vehicle manufacturing, engine and machine engineering, surface hardenable (e.g. crankshafts, bolts, transmission parts). Lowest application temp. -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm³Mecha

Steel CK 45 is suitable for mean strained parts of higher dimensions (heavy forged parts) and complexer forms in vehicle manufacturing and machine engineering (e.g. ship shafts, transmission parts, wheel hubs). Lowest application temp. -25 °C, favorable creep behaviour up to 480 °C.PropertiesGeneral

Steel CK 45 is suitable for mean strained parts of higher dimensions (heavy forged parts) and complexer forms in vehicle manufacturing and machine engineering (e.g. ship shafts, transmission parts, wheel hubs). Lowest application temp. -25 °C, favorable creep behaviour up to 480 °C.PropertiesGeneral

Steel CK 35 is suitable for a little higher strained parts in vehicle manufacturing and machine engineering with higher dimensions (heavy forged parts) and complexer forms as well as higher uniformity requirements on qualities and surface appearance (e.g. transmission parts, crankshafts). Lowest app

Steel CK 35 is suitable for a little higher strained parts in vehicle manufacturing and machine engineering with higher dimensions (heavy forged parts) and complexer forms as well as higher uniformity requirements on qualities and surface appearance (e.g. transmission parts, crankshafts). Lowest app

Steel C 60 is suitable for high ductility parts and parts of increased wear resistance requirements in vehicle manufacturing, engine and machine engineering surface hardenable (e.g. transmission parts, shafts, axles). Additional application in tooling. Lowest application temp. -25 °C.PropertiesGene

Steel C 60 is suitable for high ductility parts and parts of increased wear resistance requirements in vehicle manufacturing, engine and machine engineering surface hardenable (e.g. transmission parts, shafts, axles). Additional application in tooling. Lowest application temp. -25 °C.PropertiesGene

Steel C 45 is suitable for mean strained parts in vehicle manufacturing, engine and machine engineering (e.g. transmission shafts, gear wheels, transmission parts). Lowest application temp. -25 °C, favorable creep behaviour up to 480 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm

Steel C 45 is suitable for mean strained parts in vehicle manufacturing, engine and machine engineering (e.g. transmission shafts, gear wheels, transmission parts). Lowest application temp. -25 °C, favorable creep behaviour up to 480 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm

Steel C 35 is suitable for parts in vehicle manufacturing, engine and machine engineering with a little higher strength requirements and still low ductility requirements (e.g. gears, bolts, clutch parts). Lowest application temp. -25 °C, favorable creep behaviour up to 480 °C.PropertiesGeneralProper

Steel C 35 is suitable for parts in vehicle manufacturing, engine and machine engineering with a little higher strength requirements and still low ductility requirements (e.g. gears, bolts, clutch parts). Lowest application temp. -25 °C, favorable creep behaviour up to 480 °C.PropertiesGeneralProper

Steel 34 CrMo 4 is suitable for parts of high strength and ductility requirements at mean and higher heat-treatment sections (also heavy forged parts) in vehicle manufacturing, engine and machine engineering (e.g. shafts, wheel gears, steering knuckles). The steel shows a high specific mechanical r

The steel 80CrV2 is used as cold rolled strip for springs and special applications in thicknesses of up to 6 mm and as tempered cold strip in thicknesses from 0.30 to 3.00 mm.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.81 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100

The steel 102Cr6 is used as cold rolled strip for springs and special applications in thicknesses of up to 6 mm and as tempered cold strip in thicknesses from 0.30 to 3.00 mm.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.81 g/cm³MechanicalPropertyTemperatureValueElastic modulus-100.0 °C21

G-X 6 CrNiMo 18 10, for armatures, pumps, mixers, filters, vessels for the chemical industry, textile industry, rayon industry, cellulose industryPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.9 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C195 GPaTypical for Austenit

G-X 6 CrNi 18 9, forarmatures, pumps, centrifuges, mixers, parts for the food processing industry, dairy industry, beverages and packaging industry.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.9 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C195 GPaTypical for Austen

G-X 5 CrNiNb 18 9, for casting parts in the food processing industry, photo industry, soap producing-, textile and paper industry, salpeter acid industry, ic resistantPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.9 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C195 GP

High temperature, corrosion and acid resistant steel up to an operating temperature of 500 °C. Application: turbine blades, valve cones, hot steam valve seatsPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.76 g/cm³MechanicalPropertyTemperatureValueElastic modulus20.0 °C217.68 - 218 GPa100.0

Hardenable austenitic high temperature steel with addition of B to increase high temperature strength, the creep behaviour and the neutrons absorption. High temperature strength up to 650 °C, resistance to scaling up to 750 °C. Application: for nuts and screws, steam and gas turbines, in the chemica

High-temperature resistant steel with high-temperature strength up to 580°C for temperature loaded constructions, for srews and nutsPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.7 - 7.76 g/cm³MechanicalPropertyTemperatureValueElastic modulus20.0 °C216 - 218 GPa100.0 °C209 - 213 GPa200.0 °