Steel C25R is suitable for low strained parts in vehicle manufacturing and machine engineering which have to meet higher demands on workability while maintaining mechanical properties (e.g. transmission parts, crankshafts, cylinder). Lowest working temperature -25 °C.PropertiesGeneralPropertyTempera

Steel C25E is suitable for low strained parts of higher dimension and more complex form as well as higher demands on uniformity of proprties and surface appearance (e.g. transmission parts, crankshafts). Lowest working temperature -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.82 -

G-AlSi9Cu3 is universally used alloy with very good casting characteristics. It is characterised by less inclination to breaking in and to cavities and is mostly not hardened. The alloy is suitable for difficult shapes, thin-walled, pressure tight, oscillating loaded, impact loaded cast parts. Appli

The alloy AlCu2,5Mg0,5 (see also AlCu2,5Mg0,5, mat. No 3.1305,DIN 1725, part 1, 02.83) pertains to alloy-type (AlCuMg-type) which was used as the first of aluminium wrought materials in technics. The alloy is natural and artificial agable and achieves high mechanical strength. In soft condition the

The material GD-ZnAl4Cu1, material NR. 2.2141, characteristic Z 410, is the advantages alloy for pieces of die casting. The alloy combine good mechanical characteristics, good corrosion resistance, good dimensional accuracy and dimensional stability as well as the possibility for galvanically deposi

The material GD-ZnAl4, material NR. 2.4140, characteristic Z 400, one uses for diecastings. If there are high requirements to the accuracy to size of the products produced by diecasting, this alloy should be preferred. The material is substantially more ductile than the other high quality casting al

The material G-ZnAl6Cu1, material NR. 2.2161, characteristic Z 610, one uses for castingtechnically difficult sand and ingot castings.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C6.5 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus20.0 °C130 GPaElongation20.0 °C1 - 3 %Hardness

The material G-ZnAl4Cu3, material NR. 2.2143, characteristic Z 430, becomes application for sand castings and of ingot castings of all kinds, sheet material-forming tools as well as for injection moulding -, blowing and deep-drawing forms for plastics. The alloy Z 430 is a possible alternative to Z

Steel C15E is suitable for parts of slightly higher core strength, increased wear strain as well as of higher dimension and complexer form than standard mark C15 in vehicle manufacturing and machine engineering (e.g. levers, joints, gear wheels).PropertiesGeneralPropertyTemperatureValueDensity20.0 °

Steel C10E is suitable for lower dimension parts of low core strength and increased wear load as well as for parts of higher dimension and complexer forms than standard mark C10 in vehicle manufacturing and machine engineering (e.g. levers, bushings, molded and stamped parts).PropertiesGeneralProper

The patented cold drawn steel wire type B made of unalloyed steel is used for coil springs (tension springs, compression springs, torsion springs), spring rings and other springs with for medium static and low dynamic load.PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³

The steel Ck 15 is used for increased wear loaded parts with higher core strength in the vehicle and mechanical engineering as well as for parts of larger dimension and complexer shape as the base grade C 15 (e.g. levers, joints, gears). The lowest application amounts to -25 °C.PropertiesGeneralProp

The steel Ck 10 is used for smaller wear loaded parts with low core strength in the vehicle and mechanical engineering as well as for parts of larger dimension and complexer shape as the base grade C 10 (e.g. pins, bushes, compression mouldings and stampings). The lowest application amounts to -25 d

The steel C 15 is used for wear loaded parts with a little higher core strength in the vehicle and mechanical engineering (e.g. lever, joints, bushes, gears). The lowest application amounts to -25 °C, the best application from 5 to 10 mm nominal size. As bright steel product it is used in the form o

The steel C 10 is used for wear loaded parts with low core strength in the vehicle and mechanical engineering (e.g. pins, lever, compression mouldings and stampings). The lowest application amounts to -25 °C, the best application from 5 to 10 mm nominal size. As bright steel product it is used in th

Aluminum SAE 5005 is a lean aluminum magnesium alloy with low density and excellent thermal conductivity. This medium strength non-heat-treatable alloy is known for its corrosion resistance in alkaline marine situations. Aluminum SAE 5005 is readily machinable, and can be welded using TIG and MIG me

Steel C22E is suitable for low strained components of higher dimensions (heavy forged parts) and more complex forms as well as higher demands on uniformity of qualities and surface appearance in vehicle and machine engineering (e.g. transmission parts, crankshafts).PropertiesGeneralPropertyTemperatu

As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 -

As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentElastic modulus23.0 °C200 -

The free cutting case hardening steel 15SMn13 is applicated for turned part production. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical