PropertiesGeneralPropertyValueCommentDensity2.7 g/cm³Typical for Wrought 6000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumElongation12.0 %T42ASTM B241Tube14.0 %T42ASTM B241TubeA50Plane-Strain Fracture To

PropertiesGeneralPropertyValueCommentDensity2.7 g/cm³Typical for Wrought 6000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumElongation12.0 %T4, T4510, T4511ASTM B241Tube14.0 %T4, T4510, T4511ASTM B241TubeA

PropertiesGeneralPropertyValueCommentDensity2.7 g/cm³Typical for Wrought 6000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumElongation14.0 %OASTM B241Tube16.0 %OASTM B241TubeA50Plane-Strain Fracture Toughn

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentCharpy impact energy23.0 °C20 JElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A5023.0 °C22 %Poisson's ratio23.0 °C0.29 [-]

PropertiesGeneralPropertyValueCommentDensity2.75 - 2.84 g/cm³Typical for Wrought 2000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus70.0 - 73.0 GPaTypical for Wrought 2000 Series AluminiumElongation16.0 %T4ASTM B316Wire, RodPlane-Strain Fracture Toughnes

PropertiesGeneralPropertyValueCommentDensity2.7 g/cm³Typical for Wrought 4000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus69.0 - 71.0 GPaTypical for Wrought 4000 Series AluminiumElongation3.0 %T86ASTM B211Bar, Rod, Wire4.0 %T86ASTM B211Bar, Rod, WireA5

PropertiesGeneralPropertyValueCommentDensity2.65 - 2.7 g/cm³Typical for Wrought 5000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus69.0 - 70.0 GPaTypical for Wrought 5000 Series AluminiumElongation18.0 %OASTM B211Bar, Rod, Wire20.0 %OASTM B211Bar, Rod, W

PropertiesGeneralPropertyTemperatureValueCommentDensity23.0 °C7.8 - 7.9 g/cm³Typical for Low Carbon SteelMechanicalPropertyTemperatureValueCommentCharpy impact energy23.0 °C27 - 41 JElastic modulus23.0 °C200 - 215 GPaTypical for Low Carbon SteelElongation A20023.0 °C21 %Elongation A5023.0 °C24 %Pois

PropertiesGeneralPropertyValueCommentDensity2.65 - 2.7 g/cm³Typical for Wrought 5000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus69.0 - 70.0 GPaTypical for Wrought 5000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought

PropertiesGeneralPropertyValueCommentDensity2.7 g/cm³Typical for Wrought 6000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumElongation8.0 %T6, T6510, T6511ASTM B241TubeA509.0 %T6, T6510, T6511ASTM B241Tube

PropertiesGeneralPropertyValueCommentDensity2.7 g/cm³Typical for Wrought 6000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumElongation6.0 %T5, T5510, T5511ASTM B241Tube7.0 %T5, T5510, T5511ASTM B241TubeA50

PropertiesGeneralPropertyValueCommentDensity2.65 - 2.7 g/cm³Typical for Wrought 5000 Series AluminiumMechanicalPropertyValueConditionRelated StandardsShapeCommentElastic modulus69.0 - 70.0 GPaTypical for Wrought 5000 Series AluminiumPlane-Strain Fracture Toughnes22.0 - 35.0 MPa·√mTypical for Wrought

The cold-upsettable steel Cq 45 can be cold-formed with a low to medium rate of forming according to the usual forming methods on single-stage and multi-stage presses. BEcause of its unfavourable processing properties, Cq 45 should be replaced with steel 35 B 2. It is used for normed screws of stren

The cold-upsettable steel Cq 35 can be cold-formed with a medium rate of forming according to the usual forming methods on single-stage and multi-stage presses. It is used, for example, for screws in the lower dimension range as well as for nuts of strength class 8.8.PropertiesGeneralPropertyTempera

Steel Cm 60 is suitable for high strained parts in vehicle manufacturing, engine and machine engineering that require an enhanced workability while maintaining strength qualities (e.g. gear wheels, pinion, shafts). Lowest application temp. -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0

Steel Cm 45 is suitable for mean strained parts in vehicle manufacturing, engine and machine engineering with enhanced workability and constant mechanical qualities (e.g. transmission shafts, gear wheels, clutch parts, bolts). Lowest application temp. -25 °C.PropertiesGeneralPropertyTemperatureValue

Steel Cm 45 is suitable for mean strained parts in vehicle manufacturing, engine and machine engineering with enhanced workability and constant mechanical qualities (e.g. transmission shafts, gear wheels, clutch parts, bolts). Lowest application temp. -25 °C.PropertiesGeneralPropertyTemperatureValue

Steel Cm 35 is suitable for a little higher strained parts of enhanced workability and constant mechanical qualities in vehicle manufacturing, engine and machine engineering (e.g. transmission parts, crankshafts, cylinder). Lowest application temp. -25 °C.PropertiesGeneralPropertyTemperatureValueDen

Steel Cm 35 is suitable for a little higher strained parts of enhanced workability and constant mechanical qualities in vehicle manufacturing, engine and machine engineering (e.g. transmission parts, crankshafts, cylinder). Lowest application temp. -25 °C.PropertiesGeneralPropertyTemperatureValueDen

Steel C 60 is suitable for larger parts (heavy forged parts) and high load in vehicle manufacturing, engine and machine engineering, surface hardenable (e.g. crankshafts, bolts, transmission parts). Lowest application temp. -25 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm³Mecha