CuZn15 (CW502L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn10. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderately cold forming: go

Steel P355N is a weldable fine-grained construction steel (alloyed high-quality steel) for pressure vessel construction.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GP

Seamless tubes of the high-temperature 13CrMo4-5 are used in steam boiler and pipeline construction, pressure vessel and apparatus engineering, especially in chemical industry and power station construction. The total load and the special scaling circumstances can decrease or increase the temperatur

The ferritic steel X2CrTiNb18 is a structural stabilized stainless steel. The material is acc. to DIN EN 10095 allowed to be used as a heat-resistant steel. Application: vehicle construction, exhaust system components, whiteware, for welded parts in dairy and food industry, in breweriesPropertiesGen

Material CuZn39Sn1 (CW719R) is like make CuZn38Sn1As (CW717R) comparable to the DIN-make CuZn38Sn1 (2.0530). Similar processing properties and uses like CW717R due to the nearly identical chemical composition.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.35 - 8.4 g/cm³MechanicalPropertyTe

CuSn6, mat. No. CW425K, is comparable to the DIN-make CuSn6, mat. No. 2.1020, acc. to DIN 17662 : 1983-12. Properties of the CuSn-alloy are predominantly determined by the tin-content. Tensile strength, yield point and hardness increase according to the rising cold forming grade, elongation after fr

The austenitic steel X2CrNiMoN18-12-4 is available in solution annealed condition in the form of cold rolled band, warm rolled band and warm rolled sheet. It shows resistance to intercrystalline corrosion even in sensitized condition.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8 g/cm³Mech

Cuco2Be, mat. No CW104C, is counted among hardenable, low alloyed copper alloys. To the comparable make Cuco2Be, mat. No 2.1285, acc. to DIN 17666 : 1983-12 applies: CuCo2Be achieves compared to CuBe2 at slightly lower hardness and strength values higher electrical and thermal conductivity. The temp

The weather resistant steel S355J2WP with improved atmospheric corrosion resistance (by generation of an conversion coating) has a minimum yield strength of 355 N/mm². It is applicated for welded, screwed and riveted constructions, e.g. structural engineering, bridge building, tank construction, exh

The austenitic steel X2CrNiMo17-12-3 is applicated in solution annealed condition as cold rolled strip an hot rolled strip and sheet, wire rod and profiles. It shows resistance to intercrystalline corrosion even in sensitized condition.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8 g/cm³Me

The austenitic steel X1CrNiMoN25-25-5 is applicated in solution annealed condition as hot rolled sheet, wire rod and profiles. It shows resistance to intercrystalline corrosion even in sensitized condition.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.1 g/cm³MechanicalPropertyTemperatureV

The austenitic steel X1CrNiMoCuN20-18-7 will be delivered solution annealed as cold rolled strip, hot rolled strip and sheet, bars, wire rod and profiles. It shows resistance to intercrystalline corrosion even in sensitized condition.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8 g/cm³Mech

Cu-DLP, mat. No CW023A, is a deoxidized copper with limited, low residual copper-content. To the comparable DIN-make SW-Cu, mat. No 2.0076 acc. to DIN 1787 : 1973-01 applies: Tensile strength and Brinell hardness are increasable by cold forming. SW-Cu is hydrogen resistant and shows the lowest therm

High temperature steel for high pressure hydrogenation vessels up to 600 °C. It is scale resistant in air and steam up to 700 °C. Application: in the chemical industry, steam vessel and turbine construction for blades, screws and other high temperature partsPropertiesGeneralPropertyTemperatureValueD

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueElastic modulus-100.0 °C217 GPa20.0 °C210 - 212 GPa100.0 °C205 - 207 GPa200.0 °C195 - 199 GPa300.0 °C185 - 192 GPa400.0 °C175 - 184 GPa500.0 °C175 GPa600.0 °C164 GPaElongation20.0 °C21 - 24 %Elongation

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.83 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0 °C164 GPaElongation20.0 °C21 - 24 %Elongation, transverse20.0 °C19 -

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.82 - 7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C210 - 212 GPa100.0 °C205 - 207 GPa200.0 °C195 - 199 GPa300.0 °C185 - 192 GPa400.0 °C175 - 184 GPa500.0 °C175 GPa600.0 °C164 GPaElongation20.0 °C16 -

High temperature steel for high pressure hydrogenation vessels. In the annealed condition it is resistant to high pressure hydrogen as well as to aggressive oils. Application: hydration facilities and petroleum distillation facilities for tubes, in the quenched and tempered condition also in the ves

Temperable high strength steel with good high temperature strength up to 580 °C and resistance to scaling up to 700 °C. Application: pressure vessel and pipeline construction, turbine construction, chemicals industry, reactor engineeringPropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.75 - 7

PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.85 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100.0 °C207 GPa200.0 °C199 GPa300.0 °C192 GPa400.0 °C184 GPa500.0 °C175 GPa600.0 °C164 GPaElongation20.0 °C25 %Elongation, transverse20.0 °C23 %Poiss