The heat resistant steel X12CrNi23-13, mat. No 1.4833, is resistant in air up to 1000°C (highest application temp.). Low resistance to sulfureous gases (reducing as well as oxidizing). Mean resistance to nitrogenous, oxygen deficient gases and to carburization. The material is ideal for welding acco

50 mm is for reduction of self-equilibrating stress an annealing at 850°C necessary. To material DIN EN 10095 : 1999-03 applies: The high alloyed steel shows scaling resistance up to max. 1100°C (highest application temp. in air). It has favorable resistance to alternation of oxidizing and reducing

Copper plates, sheet and circles for boilers, pressure vessels and hot water storage units.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C8.9 - 8.94 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-253.0 °C138 GPa-195.0 °C136 GPa-100.0 °C133 GPa20.0 °C128 - 132 GPa50.0 °C127 GPa

The martensitic steel grade X4CrNiMo16-5-1 acc. to DIN EN 10272 : 2001-01is used for hot and cold formed rods for pressure vessels. The material shows favorable corrosion resistance and low-temperature ductility to -200 °C. It also has high corrosion resistance particularly to water, weak acids and

The martensitic steel grade X4CrNiMo16-5-1 acc. to DIN EN 10272 : 2001-01is used for hot and cold formed rods for pressure vessels. The material shows favorable corrosion resistance and low-temperature ductility to -200 °C. It also has high corrosion resistance particularly to water, weak acids and

The martensitic steel grade X3CrNiMo13-4 acc. to DIN EN 10272 : 2001-01is used for warm and cold formed rods for pressure vessel. The steel shows favorable ductility properties and sufficient corrosion resistance in the temperature range from -60 to 300 °C. X3CrNiMo13-4 has due to the Ni-content bet

The martensitic steel grade X3CrNiMo13-4 acc. to DIN EN 10272 : 2001-01is used for warm and cold formed rods for pressure vessel. The steel shows favorable ductility properties and sufficient corrosion resistance in the temperature range from -60 to 300 °C. X3CrNiMo13-4 has due to the Ni-content bet

Propertties: - good corrosion resistance to water and steam - is able for high gloss polishing - application temperature: -40 up to 550°C Application: - for construction elements, requiring higher strengths because higher mechanical loadings - axis, parts for pumps, plunger, valve cone, nozzle pin,

Propertties: - good corrosion resistance to water and steam - is able for high gloss polishing - application temperature: -40 up to 550°C Application: - for construction elements, requiring higher strengths because higher mechanical loadings - axis, parts for pumps, plunger, valve cone, nozzle pin,

Steel C60E is usable for larger parts (heavy forged parts) and higher loaded parts in vehicle, engine and machine engineering, surface hardenable (e.g. crankshafts, bolts,transmission).As a bright steel product the steel is used in the form of bars, bright, straight, in various conditions (see DIN E

Steel C60E is usable for larger parts (heavy forged parts) and higher loaded parts in vehicle, engine and machine engineering, surface hardenable (e.g. crankshafts, bolts,transmission).As a bright steel product the steel is used in the form of bars, bright, straight, in various conditions (see DIN E

Steel C55E is usable for larger parts in vehicle, engine and machine engineering undergoing a surface hardening (e.g. gear wheels, screws, shafts).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100

Steel C55E is usable for larger parts in vehicle, engine and machine engineering undergoing a surface hardening (e.g. gear wheels, screws, shafts).PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm³MechanicalPropertyTemperatureValueCommentElastic modulus-100.0 °C217 GPa20.0 °C212 GPa100

Steel C45 is suitable for mean loaded parts of higher dimensions (large forged parts) and complexer forms in vehicle and machine engineering (e.g. ship shafts, transmission parts, wheel hubs).As a bright steel product the steel is used in the form of bars, bright, straight, in various conditions (se

Steel C45 is suitable for mean loaded parts of higher dimensions (large forged parts) and complexer forms in vehicle and machine engineering (e.g. ship shafts, transmission parts, wheel hubs).As a bright steel product the steel is used in the form of bars, bright, straight, in various conditions (se

Steel C35E is suitable for slightly higher loaded parts of higher dimensions (large forged parts) and complexer forms as well as for higher requirements to uniformity of properties and to surface quality in vehicle and machine engineering. (e.g. transmission parts, crankshafts).As a bright steel pro

Steel C35E is suitable for slightly higher loaded parts of higher dimensions (large forged parts) and complexer forms as well as for higher requirements to uniformity of properties and to surface quality in vehicle and machine engineering. (e.g. transmission parts, crankshafts).As a bright steel pro

Properites: - resistant to medium with little chloride content up to pH-value of 4,5 - similar corrosion resistance to 1.4301 (graded as high corrosion resistan) Application: - in chemical industry, screws, nuts and cold formed parts - in arcitecture for joining elements of steel group A 2 and A 4,

Properties: - 17%-Cr-steel, able for quenching and tempering - good resistance to water, weak acids, brines and stronger oxidising acids (nitric acid) - good runnability and wear properties - high polishable - danger of galling, so use different grades of quenching and tempering when slide contact -

PropertiesGeneralPropertyValueCommentDensity2.7 g/cm³Typical for Wrought 6000 Series AluminiumMechanicalPropertyTemperatureValueConditionRelated StandardsShapeCommentElastic modulus70.0 GPaTypical for Wrought 6000 Series AluminiumElongation-75.0 °C10.0 %T5DIN 1725-1Seamless TubeTransverse-75.0 °C14.