The cold-upsettable steel 38 Cr 2 can be cold-formed with a medium rate of forming according to the usual forming methods on single-stage and multi-stage presses. It is used for screws of strength class 8.8 in the lower dimension range. The steel 38 Cr 2will be replaced with steel 35 B 2.PropertiesG

The steel 17 CrNiMo 6 is used for high loaded parts in the vehicle and mechanical engineering with high demands on toughness and core strength (e.g. gear parts, drive pinions). The lowest application amounts to -60 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm³MechanicalProperty

The steel 17 CrNiMo 6 is used for high loaded parts in the vehicle and mechanical engineering with high demands on toughness and core strength (e.g. gear parts, drive pinions). The lowest application amounts to -60 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm³MechanicalProperty

The steel 17 CrNiMo 6 is used for high loaded parts in the vehicle and mechanical engineering with high demands on toughness and core strength (e.g. gear parts, drive pinions). The lowest application amounts to -60 °C.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.8 g/cm³MechanicalProperty

The steel 17 Cr 3 is used for high wear loaded smaller parts in the vehicle and mechanical engineering (e.g. camshafts, piston pins, cylinder). The lowest application amounts to -25 °C, the best application up to 25 mm nominal size.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.82 g/cm³Mec

The steel 17 Cr 3 is used for high wear loaded smaller parts in the vehicle and mechanical engineering (e.g. camshafts, piston pins, cylinder). The lowest application amounts to -25 °C, the best application up to 25 mm nominal size.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.82 g/cm³Mec

The steel 16 MnCrS 5 is used for larger parts with higher core strength and better machinability in the vehicle and mechanical engineering (e.g. gears, shafts, steering parts). The lowest application amounts to -25 °C, the best application up to 50 mm nominal size.PropertiesGeneralPropertyTemperatur

The steel 16 MnCrS 5 is used for larger parts with higher core strength and better machinability in the vehicle and mechanical engineering (e.g. gears, shafts, steering parts). The lowest application amounts to -25 °C, the best application up to 50 mm nominal size.PropertiesGeneralPropertyTemperatur

The steel 16 MnCrS 5 is used for larger parts with higher core strength and better machinability in the vehicle and mechanical engineering (e.g. gears, shafts, steering parts). The lowest application amounts to -25 °C, the best application up to 50 mm nominal size.PropertiesGeneralPropertyTemperatur

The steel 16 MnCrS 5 is used for larger parts with higher core strength and better machinability in the vehicle and mechanical engineering (e.g. gears, shafts, steering parts). The lowest application amounts to -25 °C, the best application up to 50 mm nominal size.PropertiesGeneralPropertyTemperatur

The steel 16 MnCr 5 is used for larger parts with higher core strength and advantageous toughness properties in the vehicle and mechanical engineering (e.g. gears, shafts, steering parts). The lowest application amounts to -25 °C, the best application up to 50 mm nominal size.PropertiesGeneralProper

The steel 16 MnCr 5 is used for larger parts with higher core strength and advantageous toughness properties in the vehicle and mechanical engineering (e.g. gears, shafts, steering parts). The lowest application amounts to -25 °C, the best application up to 50 mm nominal size.PropertiesGeneralProper

The steel 16 MnCr 5 is used for larger parts with higher core strength and advantageous toughness properties in the vehicle and mechanical engineering (e.g. gears, shafts, steering parts). The lowest application amounts to -25 °C, the best application up to 50 mm nominal size.PropertiesGeneralProper

The steel 16 MnCr 5 is used for larger parts with higher core strength and advantageous toughness properties in the vehicle and mechanical engineering (e.g. gears, shafts, steering parts). The lowest application amounts to -25 °C, the best application up to 50 mm nominal size.PropertiesGeneralProper

The steel 15 CrNi 6 is used for parts in the vehicle and mechanical engineering with medium strength and high toughness (e.g. gears, shafts). The lowest application amounts to -60 °C, the best application up to 100 mm nominal size.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.84 g/cm³Mech

The steel 15 CrNi 6 is used for parts in the vehicle and mechanical engineering with medium strength and high toughness (e.g. gears, shafts). The lowest application amounts to -60 °C, the best application up to 100 mm nominal size.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.84 g/cm³Mech

The steel 15 CrNi 6 is used for parts in the vehicle and mechanical engineering with medium strength and high toughness (e.g. gears, shafts). The lowest application amounts to -60 °C, the best application up to 100 mm nominal size.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.84 g/cm³Mech

The steel 15 CrNi 6 is used for parts in the vehicle and mechanical engineering with medium strength and high toughness (e.g. gears, shafts). The lowest application amounts to -60 °C, the best application up to 100 mm nominal size.PropertiesGeneralPropertyTemperatureValueDensity20.0 °C7.84 g/cm³Mech

G-X 40 NiCrSiNb 38 18, for parts for high resistance against variation of temperature, delivering grates, bearing racks, bearing arms, parts of reeling plant oven, like drums, blades and shield etc.. Especially applicable for parts of oven in carborising atmosphere. resistance: - in oxidising burnin

G-X 40 CrSi 17, basically for parts of oven for medium mechanical loadings, like widdle grate, rods for grates, pipe clamp and pipe connexion, distance plates, far jet nozzles. In cement industry for protecting rings and protecting archs, segments etc., for cased insert box and attachments for super